Polymerizable liquid crystal composition and homeotropically-aligned liquid crystal film

ABSTRACT

A polymerizable liquid crystal composition is provided that can contains a mixture of polymerizable compounds containing a compound represented by the formula (1-1), a compound represented by the formula (2), a compound represented by the formula (3-1) and a compound represented by the formula (4), and a amine silane coupling agent. The composition can form a polymerizable liquid crystal layer exhibiting a uniform homeotropic alignment by coating the composition on a supporting substrate, independently from the kind of the supporting substrate without a special alignment film. Examples of each of the components are shown below, in which ring T represents triptycen-1,4-diyl.

FIELD OF THE INVENTION

The present invention relates to a polymerizable liquid crystal composition containing a polymerizable triptycene derivative, a homeotropically-aligned liquid crystal film obtained from the composition, use thereof and the like.

BACKGROUND OF THE INVENTION

A polymer having such a function as optical compensation can be obtained by polymerizing a polymerizable compound having a liquid crystal phase. The function is exhibited by fixing the alignment of the liquid crystal molecules through polymerization. Several polymerizable compounds are developed for utilizing such the function of polymerizable compound. However, the function may not be sufficiently exhibited with only one kind of polymerizable compound. Accordingly, such attempts have been made that a composition is prepared with plural kinds of polymerizable compounds, and the composition is polymerized to provide a polymer (see JP-H10-319408-A (GB 2324382A), JP-2004-198478-A, JP-2002-243942-A and JP-2005-196221-A).

In this specification, the fact that a liquid crystal skeleton has an alignment state, such as a homogeneous alignment, a tilted alignment, a homeotropic alignment, a twisted alignment or the like may be referred to as “having a homogeneous alignment”, “having a tilted alignment”, “having a homeotropic alignment”, “having a twisted alignment” or the like, respectively. For example, a liquid crystal film having a homeotropic molecular alignment, i.e., a homeotropically-aligned liquid crystal film, may be referred to as a liquid crystal film having a homeotropic alignment or a homeotropically-aligned liquid crystal film.

A polymer having a homeotropic alignment has an optical axis in the n_(z) direction, and the refractive index in the direction of the optical axis is larger than the refractive index in the direction perpendicular to the optical axis. Accordingly, the polymer is classified into a positive C plate in terms of optical ellipsoid. The positive C plate can be applied, by combining with a film having an other optical function, to optical compensation of a liquid crystal mode with a horizontal alignment, i.e., a so-called IPS (in-plane switching) mode, and the like, such as improvement in viewing angle characteristics of a polarizing plate (as described in M. S. Park, et al., IDW, '04, FMCS-4, M. Nakata, et al., SID, '06, P-58, K. J. Kim, et al., SID, '06, Digest, p. 1158-1161, WO 05/038517 A1 and US 2006/0182900 A1).

In the aforementioned use, there are case where the polymerizable liquid crystal material is laminated on a glass substrate, a glass substrate having coated on the surface thereof a plastic thin film (such as an overcoated film formed on a color filter), a color filter substrate (see JP-2005-164962-A) or a plastic substrate. Examples of a material used as the plastic substrate include such polymers as TAC (triacetyl cellulose), polycarbonate, PET (polyethylene terephthalate) and a cycloolefin resin.

The inventors have found a polymerizable liquid crystal composition that can form a uniform homeotropic alignment on a glass substrate or a plastic substrate with good adhesion without an alignment film formed on the substrate (see JP-2006-126757-A and JP-2007-16213-A). However, the composition may sometimes be difficult to control the optical characteristics thereof, particularly birefringence (Δn) and thus leave room for improvement. As a method for controlling birefringence, utilization of a compound having an aromatic ring in the short axis direction of mesogen (a compound having a triptycene ring) has been proposed, but it is still difficult to form a uniform homeotropic alignment only by the proposal (see JP-2006-111571-A).

SUMMARY OF THE INVENTION

An object of the invention is to provide a polymerizable liquid crystal composition containing a polymerizable triptycene derivative that is capable of forming a uniform homeotropic alignment by coating on a supporting substrate having been subjected to an alignment treatment, such as a transparent plastic film, a color filter and glass. Another object of the invention is to provide a liquid crystal layer that is controlled in alignment containing the polymerizable liquid crystal composition, a liquid crystal film containing the polymerizable liquid crystal composition having been polymerized, and an optically compensation film containing the liquid crystal film. Still another object of the invention is to provide an image display device, such as a liquid crystal display device, an organic EL display device and a plasma display device (PDP), containing the optically compensation film.

The inventors have found that stability of a homeotropic alignment state is controlled, and birefringence can be effectively controlled, by using a polymerizable triptycene derivative and a polymerizable compound having a bisphenol skeleton as components of a polymerizable liquid crystal composition and further combining a specific silane coupling agent, and thus the invention has been completed. The polymerizable triptycene derivative has at least one acryloyloxy group and can be polymerized as similar to a polymerizable liquid crystal compound. A polymer obtained from the polymerizable liquid crystal composition exhibits a uniform homeotropic alignment, and the same advantages can be obtained by coating the polymerizable liquid crystal composition on a supporting substrate having been subjected to a mechanical surface treatment, such as rubbing, or a chemical surface treatment.

BRIEF DESCRIPTION OF THE DRAWING

FIG. 1 is a diagram showing measurement results of retardation of a liquid crystal film of Example 1.

DETAILED DESCRIPTION OF THE INVENTION

The terms used in this specification will be explained. The term “liquid crystal compound” is a generic term for a compound having a liquid crystal phase and a compound having no liquid crystal phase but being useful as a component of a liquid crystal composition. The term “liquid crystal phase” means a nematic phase, a smectic phase, a cholesteric phase and the like, and means a nematic phase in many cases. The term “polymerizability” means a capability of providing a polymer through polymerization of a monomer by means of light, heat, a catalyst or the like. A compound represented by the formula (1-1) may be referred to as a compound (1-1). Compounds represented by the other formulae may be referred in the similar manner. The term “arbitrary” used upon defining the chemical structural formulae means that not only the position but also the number may be arbitrarily determined. The term “(meth)acrylic acid” is a generic term for acrylic acid and methacrylic acid. The term “(meth)acrylate” is a generic term for acrylate and methacrylate. The term “a (meth)acryloyloxy” is a generic term for an acryloyloxy group and a methacryloyloxy group.

The term “arbitrary” used in the definition of the chemical formulae means that not only an arbitrary position but also an arbitrary number. For example, the expression “arbitrary A may be replaced by B, C, D or E” includes the meanings “one of A may be replaced by B, C, D or E” and “plural A may be replaced by one of B, C, D or E”, and also includes the meaning “at least two of A replaced by B, A replaced by C, A replaced by D, and A replaced by E may be present simultaneously”. However, the expression “arbitrary —CH₂— may be replaced by —O—” does not include the case providing a bonding group —O—O—.

In the chemical structural formulae, a group represented by a symbol containing a letter (such as “A”) surrounded by a hexagon means a group having a ring structure (ring A).

A substituent shown without a specific bonding position to carbon constituting a ring means that the substituent may be bonded to the ring at an arbitrary position that is chemically possible.

In the case where the same symbol is used in plural formulae, the groups represented by the symbol have the same definition, but all the groups in the formulae may not the same group simultaneously. In other words, the same group may be selected for the plural formulae, or different groups may be selected for the plural formulae respectively.

The invention includes embodiments shown in the items [1] to [18] below.

[1] A polymerizable liquid crystal composition containing a mixture of polymerizable compounds containing at least one compound selected from a group of compounds represented by the formula (1-1) as a component A, at least one compound selected from a group of compounds represented by the formula (2-1) or at least one compound selected from a group of compounds represented by the formulae (2-2) to (2-4) as a component B, at least one compound selected from a group of compounds represented by the formula (3-1) as a component C and at least one compound selected from a group of compounds represented by the formulae (4-1) to (4-3) as a component D, and at least one compound selected from a group of compounds represented by the formulae (5-1) and (5-2) as a component E:

wherein

in the formula (1-1),

ring T represents triptycen-1,4-diyl; Z¹ independently represents hydrogen, fluorine, chlorine, methyl or trifluoromethyl; W¹ independently represents hydrogen, halogen, alkyl having from 1 to 3 carbon atoms or fluoroalkyl having from 1 to 3 carbon atoms; Y¹ independently represents a single bond, —COO—, —OCO—, —CH═CH—COO—, —OCO—CH═CH—, —(CH₂)₂—COO— or —OCO—(CH₂)₂—; and n1 independently represents an integer of from 2 to 15,

in the formula (2-1),

Z² independently represents hydrogen, fluorine, methyl or trifluoromethyl; W² independently represents hydrogen, halogen, alkyl having from 1 to 3 carbon atoms or fluoroalkyl having from 1 to 3 carbon atoms; Y² independently represents a single bond, —CH═CH— or —(CH₂)₂—; and n2 independently represents an integer of from 2 to 15,

in the formula (2-2),

L^(1a) and L^(1b) each independently represent alkyl having from 1 to 4 carbon atoms; R^(2a) and R^(2b) each independently represent alkylene having from 2 to 4 carbon atoms; Z²² independently represents hydrogen or methyl; k1 and k2 each independently represent an integer of from 0 to 4; and m22 and n22 each independently represent an integer of from 0 to 6,

in the formula (2-3),

Z²³ independently represents hydrogen or methyl; R^(3a) and R^(3b) each independently represent hydrogen, methyl or ethyl; and m23 and n23 each independently represent an integer of from 0 to 3,

in the formula (2-4),

Z²⁴ independently represents hydrogen or methyl; R^(4a) and R^(4b) each independently represent hydrogen or alkyl having from 1 to 6 carbon atoms; L^(2a) and L^(2b) each independently represent alkyl having from 1 to 6 carbon atoms; m24 and n24 each independently represent an integer of from 1 to 3; m25 and n25 each independently represent an integer of from 1 to 3; and j1 and j2 each independently represent an integer of from 0 to 4,

in the formula (3-1),

Z³ represents hydrogen, fluorine, methyl or trifluoromethyl; W³ independently represents hydrogen, halogen, alkyl having from 1 to 3 carbon atoms or fluoroalkyl having from 1 to 3 carbon atoms; X³ represents a single bond, —O—, alkylene having from 1 to 20 carbon atoms, —COO— or —OCO—; ring A³ represents 1,4-phenylene or 1,4-cyclohexylene; R³ represents hydrogen, fluorine, chlorine, cyano, alkyl having from 1 to 20 carbon atoms or alkoxy having from 1 to 20 carbon atoms, in which in the alkyl and the alkoxy, arbitrary hydrogen may be replaced by fluorine; n3 represents an integer of from 0 to 20; and p and q each independently represent 0 or 1, provided that when n3 is 0, X³ represents a single bond or alkylene having from 1 to 20 carbon atoms,

in the formulae (4-1) to (4-3),

Z⁴ independently represents hydrogen, fluorine, methyl or trifluoromethyl; W⁴ independently represents hydrogen, halogen, alkyl having from 1 to 3 carbon atoms or fluoroalkyl having from 1 to 3 carbon atoms; W⁴¹ independently represents hydrogen, halogen, alkyl having from 1 to 3 carbon atoms or fluoroalkyl having from 1 to 3 carbon atoms; W⁴² independently represents hydrogen, halogen, alkyl having from 1 to 8 carbon atoms or fluoroalkyl having from 1 to 3 carbon atoms; ring A⁴ independently represents 1,4-phenylene or 1,4-cyclohexylene; X⁴¹ and X⁴² each independently represent a single bond, —COO—, —OCO—, —CH═CH—COO—, —OCO—CH═CH—, —(CH₂)₂—COO—, —OCO—(CH₂)₂—, —(CH₂)₂—, —CH₂O— or —OCH₂—; r represents 0 or 1; Y⁴ independently represents a single bond, alkylene having from 1 to 20 carbon atoms, —O—, —COO—, —OCO— or —OCOO—; and n4 independently represents an integer of from 0 to 20, provided that when n4 is 0, Y⁴ represents a single bond or alkylene having from 1 to 20 carbon atoms,

in the formulae (5-1) and (5-2),

R⁵ independently represents methyl or ethyl; n5 represents an integer of from 1 to 5; R⁵¹ represents alkyl having from 1 to 4 carbon atoms; m represents an integer of from 1 to 3; Y⁵ represents alkylene having from 1 to 10 carbon atoms; R⁵² represents hydrogen or alkyl having from 1 to 10 carbon atoms; and R⁵³ represents alkyl having from 1 to 10 carbon atoms, and

in the formula (2-1),

A² represents a divalent group represented by one of the formulae (A2-1) to (A2-19):

[2] The polymerizable liquid crystal composition according to the item [1], wherein:

in the formula (1-1),

ring T represents triptycen-1,4-diyl; Z¹ independently represents hydrogen, fluorine, methyl or trifluoromethyl; W¹ independently represents hydrogen, fluorine, methyl or trifluoromethyl; Y¹ independently represents —COO—, —OCO—, —CH═CH—COO—, —OCO—CH═CH—, —(CH₂)₂—COO— or —OCO—(CH₂)₂—; and n1 independently represents an integer of from 2 to 10,

in the formula (2-1),

A² represents a divalent group represented by one of the formulae (A2-1) to (A2-18); Z² independently represents hydrogen, fluorine, methyl or trifluoromethyl; W² independently represents hydrogen or fluorine; Y² independently represents a single bond, —CH═CH— or —(CH₂)₂—; and n2 independently represents an integer of from 2 to 10,

in the formula (2-2),

k1 and k2 are both 0; R^(2a) and R^(2b) each independently represent alkylene having from 2 to 4 carbon atoms; Z²² independently represents hydrogen or methyl; and m22 and n22 each independently represent an integer of from 0 to 6,

in the formula (2-3),

Z²³ independently represents hydrogen or methyl; R^(3a) and R^(3b) each independently represent hydrogen, methyl or ethyl; and m23 and n23 each independently represent an integer of from 0 to 3,

in the formula (2-4),

j1 and j2 are both 0; Z²⁴ independently represents hydrogen or methyl; R^(4a) and R^(4b) each represent hydrogen; m24 and n24 each independently represent an integer of from 1 to 3; and m25 and n25 each independently represent an integer of from 1 to 3,

in the formula (3-1),

Z³ represents hydrogen, fluorine, methyl or trifluoromethyl; W³ independently represents hydrogen, fluorine, methyl or trifluoromethyl; X³ represents a single bond or —O—; ring A³ represents 1,4-phenylene or 1,4-cyclohexylene; R³ represents cyano, alkyl having from 1 to 10 carbon atoms or alkoxy having from 1 to 10 carbon atoms, in which in the alkyl and the alkoxy, arbitrary hydrogen may be replaced by fluorine; n3 represents an integer of from 2 to 12; and p and q each independently represent 0 or 1,

in the formulae (4-1) to (4-3),

Z⁴ independently represents hydrogen, fluorine, methyl or trifluoromethyl; W⁴ independently represents hydrogen, fluorine, methyl or trifluoromethyl; W⁴¹ independently represents hydrogen, methyl or ethyl; W⁴² independently represents hydrogen, alkyl having from 1 to 6 carbon atoms or trifluoromethyl; ring A⁴ independently represents 1,4-phenylene or 1,4-cyclohexylene; X⁴¹ and X⁴² each independently represent a single bond, —COO—, —OCO—, —CH═CH—COO—, —OCO—CH═CH—, —(CH₂)₂—COO— or —OCO—(CH₂)₂—; r represents 0 or 1; Y⁴ independently represents a single bond, —O—, —COO—, —OCO— or —OCOO—; and n4 independently represents an integer of from 2 to 12,

in the formulae (5-1) and (5-2),

R⁵ independently represents methyl or ethyl; n5 represents an integer of from 1 to 5; R⁵¹ represents alkyl having from 1 to 4 carbon atoms; m represents an integer of from 1 to 3; Y⁵ represents alkylene having from 1 to 10 carbon atoms; R⁵² represents hydrogen or alkyl having from 1 to 10 carbon atoms; and R⁵³ represents alkyl having from 1 to 10 carbon atoms,

a ratio of the component A is from 10 to 55% by weight, a ratio of the component B is from 3 to 20% by weight, a ratio of the component C is from 10 to 50% by weight, and a ratio of the component D is from 10 to 77% by weight, based on a total weight of the mixture of polymerizable compounds containing the components A to D, and

a ratio of the component E is from 0.01 to 0.20 in terms of weight ratio based on the mixture.

[3] The polymerizable liquid crystal composition according to the item [1], wherein:

in the formula (1-1),

ring T represents triptycen-1,4-diyl; Z¹ independently represents hydrogen, fluorine, methyl or trifluoromethyl; W¹ independently represents hydrogen or fluorine; Y¹ independently represents —COO— or —OCO—; and n1 independently represents an integer of from 2 to 8,

in the formula (2-1),

A² represents a divalent group represented by one of the formulae (A2-1) to (A2-18); Z² independently represents hydrogen or methyl; W² independently represents hydrogen or fluorine; Y² independently represents a single bond, —CH═CH— or —(CH₂)₂—; and n2 independently represents an integer of from 2 to 8,

in the formula (2-2),

k1 and k2 are both 0; R^(2a) and R^(2b) each independently represent alkylene having from 2 to 4 carbon atoms; Z²² represents hydrogen; and m22 and n22 each independently represent an integer of from 0 to 6,

in the formula (2-3),

Z²³ represents hydrogen; R^(3a) and R^(3b) each represent hydrogen; and m23 and n23 each independently represent an integer of from 0 to 3,

in the formula (2-4),

j1 and j2 are both 0; Z²⁴ represents hydrogen; R^(4a) and R^(4b) each represent hydrogen; m24 and n24 each independently represent an integer of from 1 to 3; and m25 and n25 each independently represent an integer of from 1 to 3,

in the formula (3-1),

Z³ represents hydrogen or methyl; W³ independently represents hydrogen or fluorine; X³ represents a single bond or —O—; ring A³ represents 1,4-phenylene or 1,4-cyclohexylene; R³ represents cyano, alkyl having from 1 to 10 carbon atoms or alkoxy having from 1 to 10 carbon atoms, in which in the alkyl and the alkoxy, arbitrary hydrogen may be replaced by fluorine; n3 represents an integer of from 2 to 10; and p and q each independently represent 0 or 1,

in the formulae (4-1) to (4-3),

Z⁴ independently represents hydrogen or methyl; W⁴ independently represents hydrogen, fluorine, methyl or trifluoromethyl; W^(u) independently represents hydrogen or methyl; W⁴² independently represents hydrogen, alkyl having from 1 to 4 carbon atoms or trifluoromethyl; ring A⁴ represents 1,4-phenylene or 1,4-cyclohexylene; X⁴¹ and X⁴² each independently represent —COO—, —OCO—, —CH═CH—COO—, —OCO—CH═CH—, —(CH₂)₂—COO— or —OCO—(CH₂)₂—; r represents 0 or 1; Y⁴ independently represents a single bond, —O—, —COO—, —OCO— or —OCOO—; and n4 independently represents an integer of from 2 to 12,

in the formulae (5-1) and (5-2),

R⁵ independently represents methyl or ethyl; n5 represents an integer of from 1 to 5; R⁵¹ represents alkyl having from 1 to 4 carbon atoms; m represents an integer of from 1 to 3; Y⁵ represents alkylene having from 1 to 10 carbon atoms; R⁵² represents hydrogen or alkyl having from 1 to 10 carbon atoms; and R⁵³ represents alkyl having from 1 to 10 carbon atoms,

a ratio of the component A is from 15 to 55% by weight, a ratio of the component B is from 3 to 15% by weight, a ratio of the component C is from 15 to 45% by weight, and a ratio of the component D is from 15 to 67% by weight, based on a total weight of the mixture of polymerizable compounds containing the components A to D, and

a ratio of the component E is from 0.03 to 0.15 in terms of weight ratio based on the mixture.

[4] The polymerizable liquid crystal composition according to the item [1], wherein:

in the formula (1-1),

ring T represents triptycen-1,4-diyl; Z¹ represents hydrogen; W¹ independently represents hydrogen or fluorine; Y¹ independently represents —COO— or —OCO—; and n1 independently represents an integer of from 4 to 6,

in the formula (2-1),

A² represents a divalent group represented by one of the formulae (A2-1), (A2-4), (A2-10), (A2-11) and (A2-16); Z² represents hydrogen; W² independently represents hydrogen or fluorine; Y² independently represents a single bond, —CH═CH— or —(CH₂)₂—; and n2 independently represents an integer of from 4 to 6,

in the formula (2-2),

k1 and k2 are both 0; R^(2a) and R^(2b) each independently represent alkylene having from 2 to 4 carbon atoms; Z²² represents hydrogen; and m22 and n22 each independently represent an integer of from 0 to 6,

in the formula (2-3),

Z²³ represents hydrogen; R^(3a) and R^(3b) each represent hydrogen; and m23 and n23 each independently represent an integer of from 0 to 3,

in the formula (2-4),

j1 and j2 are both 0; Z²⁴ represents hydrogen; R^(4a) and R^(4b) each represent hydrogen; m24 and n24 each independently represent an integer of from 1 to 3; and m25 and n25 each independently represent an integer of from 1 to 3,

in the formula (3-1),

Z³ represents hydrogen; W³ represents hydrogen; X³ represents a single bond or —O—; ring A³ represents 1,4-phenylene; R³ represents cyano; n3 represents an integer of from 4 to 6; and p and q each independently represent 0 or 1,

in the formulae (4-1) to (4-3),

Z⁴ represents hydrogen; W⁴ independently represents hydrogen, fluorine or methyl; W⁴¹ independently represents hydrogen or methyl; W⁴² independently represents hydrogen, methyl or trifluoromethyl; ring A⁴ represents 1,4-phenylene; X⁴¹ and X⁴² each independently represent —COO—, —OCO—, —CH═CH—COO—, —OCO—CH═CH—, —(CH₂)₂—COO— or —OCO—(CH₂)₂—; r represents 0 or 1; Y⁴ independently represents a single bond or —O—; and n4 independently represents an integer of from 4 to 6,

in the formulae (5-1) and (5-2),

R⁵ independently represents methyl or ethyl; n5 represents an integer of from 1 to 5; R⁵¹ represents alkyl having from 1 to 4 carbon atoms; m represents an integer of from 1 to 3; Y⁵ represents alkylene having from 1 to 10 carbon atoms; R⁵² represents hydrogen or alkyl having from 1 to 10 carbon atoms; and R⁵³ represents alkyl having from 1 to 10 carbon atoms,

a ratio of the component A is from 20 to 45% by weight, a ratio of the component B is from 8 to 12% by weight, a ratio of the component C is from 20 to 40% by weight, and a ratio of the component D is from 20 to 52% by weight, based on a total weight of the mixture of polymerizable compounds containing the components A to D, and

a ratio of the component E is from 0.05 to 0.15 in terms of weight ratio based on the mixture.

[5] The polymerizable liquid crystal composition according to the item [1], wherein:

in the formula (1-1),

ring T represents triptycen-1,4-diyl; Z¹ represents hydrogen; W¹ independently represents hydrogen or fluorine; Y¹ independently represents —COO— or —OCO—; and n1 independently represents an integer of from 4 to 6,

in the formula (2-1),

A² represents a divalent group represented by one of the formulae (A2-10) and (A2-16); Z² represents hydrogen; W² independently represents hydrogen or fluorine; Y² independently represents a single bond, —CH═CH— or —(CH₂)₂—; and n2 independently represents an integer of from 4 to 6,

in the formula (2-2),

k1 and k2 are both 0; R^(2a) and R^(2b) each independently represent alkylene having from 2 to 4 carbon atoms; Z²² represents hydrogen; and m22 and n22 each independently represent an integer of from 1 to 4,

in the formula (2-3),

Z²³ represents hydrogen; R^(3a) and R^(3b) each represent hydrogen; and m23 and n23 each independently represent an integer of from 0 to 3,

in the formula (2-4),

j1 and j2 are both 0; Z²⁴ represents hydrogen; R^(4a) and R^(4b) each represent hydrogen; m24 and n24 each independently represent an integer of from 1 to 3; and m25 and n25 each independently represent an integer of from 1 to 3,

in the formula (3-1),

Z³ represents hydrogen; W³ represents hydrogen; X³ represents a single bond or —O—; ring A³ represents 1,4-phenylene; R³ represents cyano; n3 represents an integer of from 4 to 6; and p and q each independently represent 0 or 1,

in the formulae (4-1) to (4-3),

Z⁴ represents hydrogen; W⁴ independently represents hydrogen, fluorine or methyl; W⁴¹ independently represents hydrogen or methyl; W⁴² independently represents hydrogen, methyl or trifluoromethyl; ring A⁴ represents 1,4-phenylene; X⁴¹ and X⁴² each independently represent —COO—, —OCO—, —CH═CH—COO—, —OCO—CH═CH—, —(CH₂)₂—COO— or —OCO—(CH₂)₂—; r represents 0 or 1; Y⁴ independently represents a single bond or —O—; and n4 independently represents an integer of from 4 to 6,

in the formulae (5-1) and (5-2),

R⁵ independently represents methyl or ethyl; n5 represents an integer of from 1 to 5; R⁵¹ represents alkyl having from 1 to 4 carbon atoms; m represents an integer of from 1 to 3; Y⁵ represents alkylene having from 1 to 10 carbon atoms; R⁵² represents hydrogen or alkyl having from 1 to 10 carbon atoms; and R⁵³ represents alkyl having from 1 to 10 carbon atoms,

a ratio of the component A is from 20 to 45% by weight, a ratio of the component B is from 8 to 12% by weight, a ratio of the component C is from 20 to 40% by weight, and a ratio of the component D is from 20 to 52% by weight, based on a total weight of the mixture of polymerizable compounds containing the components A to D, and

a ratio of the component E is from 0.07 to 0.15 in terms of weight ratio based on the mixture.

[6] The polymerizable liquid crystal composition according to the item [1], wherein:

in the formulae (5-1) and (5-2),

R⁵ represents ethyl; n5 represents an integer of from 1 to 5; R⁵¹ represents methyl or ethyl; m represents 3; Y⁵ represents alkylene having from 1 to 10 carbon atoms; R⁵² represents hydrogen or alkyl having from 1 to 10 carbon atoms; and R⁵³ represents alkyl having from 1 to 10 carbon atoms.

[7] The polymerizable liquid crystal composition according to one of the items [2] to [5], wherein:

in the formulae (5-1) and (5-2),

R⁵ represents ethyl; n5 represents an integer of from 1 to 5; R⁵¹ represents methyl or ethyl; m represents 3; Y⁵ represents alkylene having from 1 to 10 carbon atoms; R⁵² represents hydrogen or alkyl having from 1 to 10 carbon atoms; and R⁵³ represents alkyl having from 1 to 10 carbon atoms, and

a ratio of the component E is from 0.07 to 0.13 in terms of weight ratio based on the mixture of polymerizable compounds containing the components A to D.

[8] A polymerizable liquid crystal layer having a homeotropic alignment obtained by directly coating the polymerizable liquid crystal composition according to one of the items [1] to [7] on a supporting substrate.

[9] The polymerizable liquid crystal layer according to the item [8], wherein the supporting substrate is a glass substrate.

[10] The polymerizable liquid crystal layer according to the item [8], wherein the supporting substrate is a glass substrate plated with a plastic thin film, or a plastic film substrate.

[11] The polymerizable liquid crystal layer according to the item [8], wherein the supporting substrate is a glass substrate which is plated with a plastic thin film and then the surface of the plastic thin film is subjected to a rubbing treatment, a corona treatment or a plasma treatment, or a plastic film substrate having a surface subjected to a rubbing treatment, a corona treatment or a plasma treatment.

[12] The polymerizable liquid crystal layer according to the item [10] or [11], wherein a plastic material constituting the plastic thin film or the plastic film is one selected from polyimide, polyamideimide, polyamide, polyetherimide, polyetheretherketone, polyetherketone, polyketonesulfide, polyethersulfone, polysulfone, polyphenylene sulfide, polyphenylene oxide, polyethylene terephthalate, polybutylene terephthalate, polyethylene naphthalate, polyacetal, polycarbonate, polyarylate, an acrylic resin, polyvinyl alcohol, polypropylene, cellulose, triacetyl cellulose, a partially saponified product of triacetyl cellulose, an epoxy resin, a phenol resin and a cycloolefin resin.

[13] The polymerizable liquid crystal layer according to the item [12], wherein a plastic material constituting the plastic thin film or the plastic film is one selected from polyimide, polyvinyl alcohol, triacetyl cellulose, a partially saponified product of triacetyl cellulose and a cycloolefin resin.

[14] A liquid crystal film having a homeotropic alignment obtained by polymerizing the polymerizable liquid crystal layer according to one of the items [8] to [13].

[15] An optical compensation device containing the liquid crystal film according to the item [14].

[16] An optical device containing the liquid crystal film according to the item [14] and a polarizing plate.

[17] A liquid crystal display device containing the optical compensation device according to the item [15] on an inner surface or an outer surface of a liquid crystal cell.

[18] A liquid crystal display device containing the optical device according to the item [16] on an outer surface of a liquid crystal cell.

The polymerizable liquid crystal composition of the invention contains the mixture of liquid crystal compounds containing the component A, the component B, the component C and the component D.

The component A is at least one compound selected from a group of compounds represented by the formula (1-1).

In the formula (1-1), ring T represents triptycen-1,4-diyl. Z¹ independently represents hydrogen, fluorine, chlorine, methyl or trifluoromethyl. Preferred examples of Z¹ include hydrogen, fluorine, methyl and trifluoromethyl, and the most preferred example thereof is hydrogen. W¹ independently represents hydrogen, halogen, alkyl having from 1 to 3 carbon atoms or fluoroalkyl having from 1 to 3 carbon atoms. Preferred examples of W¹ include hydrogen, fluorine, methyl and trifluoromethyl, and more preferred examples thereof include hydrogen and fluorine. The most preferred example of W¹ is hydrogen. Y¹ independently represents a single bond, —COO—, —OCO—, —CH═CH—COO—, —OCO—CH═CH—, —(CH₂)₂—COO— or —OCO— (CH₂)₂—. Preferred examples of Y¹ include —COO—, —OCO—, —CH═CH—COO—, —OCO—CH═CH—, —(CH₂)₂—COO— or —OCO—(CH₂)₂—, and more preferred examples thereof include —COO— and —OCO—. n1 independently represents an integer of from 2 to 15. n1 preferably represents an integer of from 2 to 10, more preferably an integer of from 2 to 8, and most preferably an integer of from 4 to 6.

The component B is at least one compound selected from a group of compounds represented by the formulae (2-1) to (2-4)

In the formula (2-1), A² represents a divalent group represented by one of the formulae (A2-1) to (A2-19):

Preferred examples of A² include the groups represented by the formulae (A2-1) to (A2-18), more preferred examples thereof include the groups represented by the formulae (A2-1), (A2-4), (A2-10), (A2-11) and (A2-16), and particularly preferred examples thereof include the groups represented by the formulae (A2-10) and (A2-16).

In the formula (2-1), Z² independently represents hydrogen, fluorine, methyl or trifluoromethyl. Preferred examples of Z² include hydrogen and methyl, and the most preferred example thereof is hydrogen. W² independently represents hydrogen, halogen, alkyl having from 1 to 3 carbon atoms or fluoroalkyl having from 1 to 3 carbon atoms. Preferred examples of W² include hydrogen and fluorine. Y² independently represents a single bond, —CH═CH— or —(CH₂)₂—, and preferably represents a single bond. n2 independently represents an integer of from 2 to 15. n2 preferably represents an integer of from 2 to 10, more preferably an integer of from 2 to 8, and particularly preferably an integer of from 4 to 6.

In the formula (2-2), L^(1a) and L^(1b) each independently represent alkyl having from 1 to 4 carbon atoms. R^(2a) and R^(2b) each independently represent alkylene having from 2 to 4 carbon atoms. Z²² independently represents hydrogen or methyl, and preferably represents hydrogen. k1 and k2 each independently represent an integer of from 0 to 4, and preferably are both 0. m22 and n22 each independently represent an integer of from 0 to 6, and preferably an integer of from 1 to 4.

In the formula (2-3), Z²³ independently represents hydrogen or methyl, and preferably represents hydrogen. R^(3a) and R^(3b) each independently represent hydrogen, methyl or ethyl, and preferably represents hydrogen. m23 and n23 each independently represent an integer of from 0 to 3.

In the formula (2-4), Z²⁴ independently represents hydrogen or methyl, and preferably represents hydrogen. R^(4a) and R^(4b) each independently represent hydrogen or alkyl having from 1 to 6 carbon atoms, and preferably each represent hydrogen. L^(2a) and L^(2b) each independently represent alkyl having from 1 to 6 carbon atoms. m24 and n24 each independently represent an integer of from 1 to 3. m25 and n25 each independently represent an integer of from 1 to 3. j1 and j2 each independently represent an integer of from 0 to 4, and preferably are both 0.

The component C is at least one compound selected from a group of compounds represented by the formula (3-1).

In the formula (3-1), Z³ represents hydrogen, fluorine, methyl or trifluoromethyl. Preferred examples of Z³ include hydrogen and methyl, and the most preferred example thereof is hydrogen. W³ independently represents hydrogen, halogen, alkyl having from 1 to 3 carbon atoms or fluoroalkyl having from 1 to 3 carbon atoms. Preferred examples of W³ include hydrogen, fluorine, methyl and trifluoromethyl, and the most preferred example thereof is hydrogen. X³ represents a single bond, —O—, alkylene having from 1 to 20 carbon atoms, —COO— or —OCO—. Preferred examples of X³ include a single bond and —O—. Ring A³ represents 1,4-phenylene or 1,4-cyclohexylene, and preferably represents 1,4-phenylene. R³ represents hydrogen, fluorine, chlorine, cyano, alkyl having from 1 to 20 carbon atoms or alkoxy having from 1 to 20 carbon atoms. Preferred examples of R³ include fluorine, cyano, alkyl having from 1 to 20 carbon atoms or alkoxy having from 1 to 20 carbon atoms. More preferred examples of R³ include cyano, alkyl having from 1 to 10 carbon atoms or alkoxy having from 1 to 10 carbon atoms, and the most preferred example thereof is cyano. When R³ is the alkyl or the alkoxy, arbitrary hydrogen in the group may be replaced by fluorine. n3 represents an integer of from 0 to 20, preferably an integer of from 2 to 12, more preferably an integer of from 2 to 10, and particularly preferably an integer of from 4 to 6. p and q each independently represent 0 or 1.

The component D is at least one compound selected from a group of compounds represented by the formulae (4-1) to (4-3).

In the formulae (4-1) to (4-3), Z⁴ independently represents hydrogen, fluorine, methyl or trifluoromethyl. Preferred examples of Z⁴ include hydrogen and methyl, and the most preferred example thereof is hydrogen. W⁴ independently represents hydrogen, halogen, alkyl having from 1 to 3 carbon atoms or fluoroalkyl having from 1 to 3 carbon atoms. Preferred examples of W⁴ include hydrogen, fluorine, methyl and trifluoromethyl, and more preferred examples thereof include hydrogen, fluorine and methyl. W⁴¹ independently represents hydrogen, halogen, alkyl having from 1 to 3 carbon atoms or fluoroalkyl having from 1 to 3 carbon atoms. Preferred examples of W⁴¹ include hydrogen, methyl and ethyl, and the most preferred example thereof is methyl. W⁴² independently represents hydrogen, halogen, alkyl having from 1 to 8 carbon atoms or fluoroalkyl having from 1 to 3 carbon atoms. Preferred examples of W⁴² include hydrogen, alkyl having from 1 to 6 carbon atoms and trifluoromethyl, more preferred examples thereof include hydrogen, alkyl having from 1 to 4 carbon atoms and trifluoromethyl, and particularly preferred examples thereof include hydrogen, methyl and trifluoromethyl. Ring A⁴ independently represents 1,4-phenylene or 1,4-cyclohexylene, and preferably represents 1,4-phenylene. X⁴¹ and X⁴² each independently represent a single bond, —COO—, —OCO—, —CH═CH—COO—, —OCO—CH═CH—, —(CH₂)₂—COO—, —OCO—(CH₂)₂—, —(CH₂)₂—, —C≡C—, —CH₂O— or —OCH₂—. Preferred examples of X⁴¹ and X⁴² include a single bond, —COO—, —OCO—, —CH═CH—COO—, —OCO—CH═CH—, —(CH₂)₂—COO— and —OCO—(CH₂)₂—, and more preferred examples thereof include —COO—, —OCO—, —CH═CH—COO—, —OCO—CH═CH—, —(CH₂)₂—COO— and —OCO—(CH₂)₂—. r represents 0 or 1. Y⁴ independently represents a single bond, alkylene having from 1 to 20 carbon atoms, —O—, —COO—, —OCO— or —OCOO—. Preferred examples of Y⁴ include a single bond, —O—, —COO—, —OCO— or —OCOO—, and more preferred examples thereof include a single bond and —O—. n4 independently represents an integer of from 0 to 20. When n4 is 0, Y⁴ represents a single bond or alkylene having from 1 to 20 carbon atoms. n4 preferably represents an integer of from 2 to 12, more preferably an integer of from 2 to 8, and particularly preferably an integer of from 4 to 6.

The polymerizable liquid crystal composition of the invention contains the mixture of liquid crystal compounds containing the component A, the component B, the component C and the component D, and at least one silane coupling agent selected from the group of compounds represented by the formulae (5-1) and (5-2) as the component E.

In the formulae (5-1) and (5-2), R⁵ independently represents methyl or ethyl, and preferably represents ethyl. n5 represents an integer of from 1 to 5, and preferably represents 3. R⁵¹ represents alkyl having from 1 to 4 carbon atoms, and preferably represents methyl or ethyl. m represents an integer of from 1 to 3, and preferably represents 3. Y⁵ represents alkylene having from 1 to 10 carbon atoms, and preferably represents —(CH₂)₃—. R⁵² represents hydrogen or alkyl having from 1 to 10 carbon atoms, and R⁵³ represents alkyl having from 1 to 10 carbon atoms. Preferred examples of the alkyl having from 1 to 10 carbon atoms include alkyl having from 1 to 6 carbon atoms, more preferred examples thereof include methyl, ethyl, propyl, isopropyl, butyl, isobutyl and tert-butyl, and particularly preferred examples thereof include methyl and isobutyl.

The characteristic features of the compounds used in the polymerizable liquid crystal composition of the invention will be described.

The compound (1-1) has a skeleton containing triptycene and having aromatic rings in the short axis direction of mesogen, and has two polymerizable groups. The compound (1-1) may be a compound that exhibits liquid crystallinity or a compound that does not exhibit liquid crystallinity. A polymer of the polymerizable compound can have a three-dimensional structure, and thus the compound provides a harder polymer than a compound having one polymerizable group. The compound has good compatibility with another liquid crystal compound to maintain liquid crystallinity upon using in a large amount, and has a function of decreasing the birefringence.

The compounds (2-1) to (2-4) each have a bisphenol skeleton and two polymerizable groups. A polymer of the polymerizable compounds can have a three-dimensional structure, and thus the compound provides a harder polymer than a compound having one polymerizable group. The compounds (2-1) to (2-4) each may be a compound that exhibits liquid crystallinity or a compound that does not exhibit liquid crystallinity. The compounds have a function of decreasing the melting point of the polymerizable liquid crystal composition. The use of the compound with other polymerizable liquid crystal compound facilitates formation of a homeotropic alignment while it depends on the conditions including the supporting substrate, the additives and the like. In the following description, the compounds (2-1) to (2-4) may be referred to as a compound (2) as a generic term.

The compound (3-1) has a liquid crystal skeleton and one polymerizable group. The compound (3-1) has a function of increasing the tilt angle of the other liquid crystal compounds and a function of controlling the melting point.

The compounds (4-1) to (4-3) each have a liquid crystal skeleton and two polymerizable groups. A polymer of the polymerizable compounds can have a three-dimensional structure, and thus the compounds provide a harder polymer than a compound having one polymerizable group. The compounds are liable to exhibit a homogeneous alignment while it depends on the conditions including the supporting substrate, the additives and the like. The compounds exhibit a liquid crystal phase within a wide temperature range. In the following description, the compounds (4-1) to (4-3) may be referred to as a compound (4) as a generic term.

The compounds (5-1) and (5-2) each are an amine-series silane coupling agent. The compounds have a function of enhancing adhesion to the supporting substrate and a function of facilitating formation of a homeotropic alignment. In the following description, the compounds (5-1) and (5-2) may be referred to as a compound (5) as a generic term.

The ratios of the components in the mixture of polymerizable liquid crystal compounds of the components A to D used in the composition of the invention will be described.

The ratio of the component A is preferably from 10 to 55% by weight, more preferably from 15 to 55% by weight, and further preferably from 20 to 45% by weight.

The ratio of the component B is preferably from 3 to 20% by weight, more preferably from 3 to 15% by weight, and further preferably from 8 to 12% by weight.

The ratio of the component C is preferably from 10 to 50% by weight, more preferably from 15 to 45% by weight, and further preferably from 20 to 40% by weight.

The ratio of the component D is preferably from 10 to 77% by weight, more preferably from 15 to 67% by weight, and further preferably from 20 to 52% by weight.

The polymerizable liquid crystal composition of the invention contains the mixture of the components A to D and the silane coupling agent as the component E. The ratio of the component E is preferably from 0.01 to 0.20, more preferably from 0.03 to 0.15, further preferably from 0.05 to 0.15, and particularly preferably from 0.07 to 0.13, in terms of weight ratio based on the total amount of the components A to D.

The polymerizable liquid crystal composition of the invention may contain other polymerizable compound that is different from the compound (1-1), the compound (2), the compound (3-1) and the compound (4). The amount of the other polymerizable compound added is preferably from 0 to 0.20, and more preferably from 0 to 0.10, in terms of weight ratio based on the total amount of the components A to D. The composition may contain a surfactant for forming a thin coated film. Upon adding a surfactant, however, the kind and the amount thereof are determined to prevent the homeotropic alignment from being hindered. For example, the amount of the surfactant added is preferably less than 0.0001 in terms of weight ratio based on the total amount of the components A to D. The composition may contain an additive, such as a polymerization initiator and a photosensitizer that are suitable for polymerization reaction. The composition may contain an additive, such as an ultraviolet ray absorbent, an antioxidant, a radical scavenger and a light stabilizer, for enhancing the characteristics of the polymer. Upon using the additive, the amount thereof may be the minimum amount that achieves the object of the additive. The composition may be used after dissolving in an organic solvent for forming a coated film (paint film) having a uniform thickness.

Preferred embodiments and ratios of the components of the polymerizable liquid crystal composition of the invention have been described. The items [2] to [7] above are examples of combinations of the preferred embodiments.

The composition of the invention has a nematic phase at room temperature and exhibits a homeotropic alignment on a plastic substrate, a supporting substrate having a plastic thin film coated on the surface thereof, or a glass substrate. The composition of the invention has a strong tendency to exhibit a homeotropic alignment on a supporting substrate having a polar group, such as —COOH, —NH₂ and —OH, on the surface thereof, and does not require a special alignment film for forming a homeotropic alignment (such as an alignment film having long-chain alkyl).

The synthesis methods of the compounds will be described. The compounds used in the invention can be synthesized by appropriately combining the synthesis methods in organic chemistry described, for example, in: Houben Wyle, Methoden der Organischen Chemie, Georg Thieme Valag, Stuttgart; Organic Reactions, John Wiley & Sons, Inc.; Organic Syntheses, John Wiley & Sons, Inc.; Comprehensive Organic Synthesis, Pergamon Press; and New Experimental Chemistry Course (Shin Jikken Kagaku Kouza), Maruzen, Inc.

A synthesis method of the compound (1-1) is disclosed in JP-2006-111571-A. Ring T in the formula (1-1) is a triptycene ring shown below, which can be produced, for example, by the method disclosed in P. D. Bartlett, et al., J. Am, Chem. Soc., vol. 64, p. 2649 (1942).

Synthesis methods of the compounds (2) are disclosed in the following literatures.

Compound (2-1): JP-2007-16213-A and JP-2008-133344-A

Compound (2-2): WO 2005/33061

Compound (2-3): JP-2005-338550-A

Compound (2-4): JP-2002-348357-A

A synthesis method of the compound (3-1) is disclosed in Macromolecules, vol. 26, pp. 6132-6134 (1993), Makromol. Chem., vol. 183, pp. 2311-2321 (1982), JP-2005-187618-A, JP-7-53961-A, WO 97/34862, EP 1626079 and JP-2005-179557-A.

A synthesis method of the compound (4-1) is disclosed in JP-2003-238419-A and WO 2008/136265. A synthesis method of the compound (4-2) is disclosed in Makromol. Chem., vol. 190, pp. 2255-2268 (1989), WO 97/00600 and the like. In a method for introducing α-fluoroacryloyloxy (CH₂═CF—COO—), α-fluoroacrylic acid or α-fluoroacrylic acid chloride may be used, and a method of acting α-fluoroacrylic acid fluoride (CH₂═CFCOOF) can be advantageously employed. A synthesis method of α-fluoroacrylic acid fluoride is disclosed in J. Org. Chem., vol. 54, p. 5640 (1989), JP-60-158137-A, JP-61-85345-A and the like, and α-fluoroacrylic acid fluoride can be synthesized according to the method. The compounds (4-1) and (4-2) can be synthesized from these compounds as starting materials. A synthesis method of the compound (4-3) is disclosed in JP-2004-137281-A, JP-1-271402-A, WO 2008/61606 and the like.

Examples of the component compounds will be described.

Preferred examples of the compound (1-1) include the following compounds.

In the formulae (1-1-A) to (1-1-C), Z¹ represents hydrogen, fluorine, chlorine, methyl or trifluoromethyl; W¹ represents hydrogen or fluorine; and n1 represents an integer of from 2 to 15.

Preferred examples of the compound (2-1) include the following compounds.

In the formulae (2-1-A) to (2-1-I), Z² represents hydrogen, fluorine, methyl or trifluoromethyl; W² represents hydrogen or fluorine; and n2 represents an integer of from 2 to 15.

Preferred examples of the compound (3-1) include the following compounds.

In the formulae (3-1-A) to (3-1-V), Z³ represents hydrogen, fluorine, methyl or trifluoromethyl; W³ represents hydrogen or fluorine; R³ represents alkyl having from 1 to 20 carbon atoms or —CF₃; and n3 represents an integer of from 2 to 20.

Preferred examples of the compound (4-1) include the following compounds.

Preferred examples of the compound (4-2) include the following compounds.

Preferred examples of the compound (4-3) include the following compounds.

In the formulae (4-1-A) to (4-1-H), (4-2-A) to (4-2-F), and (4-3-A) to (4-3-I), Z⁴ independently represents hydrogen, fluorine, methyl or trifluoromethyl; and n4 represents an integer of from 2 to 12.

Specific examples of the compound (1-1), the compound (2), the compound (3-1), the compound (4) and the compound (5) are shown below.

In the compound (2-3-A1), m23 and n23 have the same meanings as m23 and n23 in the formula (2-3), respectively.

In the formulae (3-1-A1) to (3-1-V2), R³ represents alkyl having from 1 to 12 carbon atoms or —CF₃.

Examples of the other polymerizable compound, the additive and the organic solvent are shown below. These compounds may commercially available products.

Examples of the other polymerizable compound include a compound having one polymerizable group, a compound having two polymerizable groups and a compound having three or more polymerizable groups.

Examples of the compound having one polymerizable group include styrene, nuclear-substituted styrene, acrylonitrile, vinyl chloride, vinylidene chloride, vinylpyridine, N-vinylpyrrolidone, vinylsulfonic acid, a vinyl fatty acid ester (such as vinyl acetate), an α,β-ethylenic unsaturated carboxylic acid (such as acrylic acid, methacrylic acid, maleic acid, fumaric acid and itaconic acid), an alkyl ester of (meth)acrylic acid (number of carbon atoms of the alkyl: 1 to 18), a hydroxyalkyl ester of (meth)acrylic acid (number of carbon atoms of the hydroxyalkyl: 1 to 18), an aminoalkyl ester of (meth)acrylic acid (carbon number of the aminoalkyl: 1 to 18), an ether oxygen-containing alkyl ester of (meth)acrylic acid (number of carbon atoms of the ether oxygen-containing alkyl: 3 to 18, such as methoxyethyl ester, ethoxyethyl ester, methoxypropyl ester, methylcarbyl ester, ethylcarbyl ester and butylcarbyl ester), N-vinylacetamide, vinyl p-t-butyl benzoate, vinyl N,N-dimethylaminobenzoate, vinyl benzoate, vinyl pivalate, vinyl 2,2-dimethylbutanoate, vinyl 2,2-dimethylpentanoate, vinyl 2-methyl-2-butanoate, vinyl propinoate, vinyl stearate, vinyl 2-ethyl-2-methylbutanoate, dicyclopentanyloxylethyl(meth)acrylate, isobornyloxyethyl(meth)acrylate, isobornyl(meth)acrylate, adamantyl(meth)acrylate, dimethyladamantyl(meth)acrylate, dicyclopentanyl(meth)acrylate, dicyclopentenyl(meth)acrylate, 2-acryloyloxyethylsuccinic acid, 2-acryloyloxyethylhexahydrophthalic acid, 2-acryloyloxyethylphthalic acid, 2-acryloyloxyethyl-2-hydroxyethylphthalic acid, 2-(meth)acryloyloxyethyl acid phosphate, a mono(meth)acrylate ester or a di(meth)acrylate ester of polyalkylene glycol having a polymerization degree of from 1 to 100, and a mono(meth)acrylate ester of polyalkylene glycol having a polymerization degree of from 1 to 100 having terminals capped with an alkyl group having from 1 to 6 carbon atoms. Examples of the polyalkylene glycol include polyethylene glycol, polypropylene glycol and a copolymer of ethylene oxide and propylene oxide.

Examples of the compound having two or more polymerizable groups include 1,4-butanediol di(meth)acrylate, 1,6-hexanediol di(meth)acrylate, 1,9-nonanediol di(meth)acrylate, neopentyl glycol di(meth)acrylate, dimethyloltricyclodecane di(meth)acrylate, triethylene glycol di(meth)acrylate, dipropylene glycol di(meth)acrylate, tripropylene glycol di(meth)acrylate, tetraethylene glycol di(meth)acryalte, bisphenol A ethylene oxide adduct di(meth)acrylate, bisphenol A glycidyl di(meth)acryalte (Biscoat V #700), polyethylene glycol di(meth)acryalte, and polymerizable bisphenol fluorenone derivatives having a cardo structure represented by the formulae (G-1) and (G-2). These compounds are suitable for enhancing the film forming capability of the polymer.

The polyfunctional compound is a non-liquid crystalline compound having from 3 to 70 polymerizable groups in one molecule. The compounds may be commercially available products. Preferred examples of the polyfunctional compound include pentaerythritol tri(meth)acrylate, trimethylolpropane tri(meth)acrylate, trimethylol ethylene oxide adduct tri(meth)acrylate, tris(meth)acryloyloxyethyl phosphate, tris((meth)acryloyloxyethyl) isocyanurate, alkyl-modified dipentaerythritol (meth)acrylate, ethylene oxide-modified trimethylolpropane (meth)acrylate, propylene oxide-modified trimethylolpropane (meth)acrylate, pentaerythritol tetra(meth)acrylate, alkyl-modified dipentaerythritol tetra(meth)acrylate, ditrimethylolpropane tetra(meth)acrylate, dipentaerythritol hexa(meth)acrylate, dipentaerythritol monohydroxypenta(meth)acrylate, alkyl-modified dipentaerythritol penta(meth)acrylate, Biscoat V #802 (number of functional groups: 8) and Biscoat V #1000 (number of functional groups: 14 in average). “Biscoat” is a trade name of the products available from Osaka Organic Chemical Industry Ltd. The polyfunctional compound having 16 or more functional groups can be obtained by acrylating Boltorn H20 (number of functional groups: 16), Boltorn H30 (number of functional groups: 32) and Boltorn H40 (number of functional groups: 64), which are available from Perstorp Speciality Chemicals.

A known photopolymerization initiator may be used for optimizing the polymerization rate of the polymerizable liquid crystal composition. The amount of the photopolymerization initiator added is preferably from 0.0001 to 0.20, more preferably from 0.001 to 0.15, and further preferably from 0.01 to 0.15, in terms of weight ratio based on the total amount of the components A to D. Examples of the photopolymerization initiator include 2-hydroxy-2-methyl-1-phenylpropan-1-one (Darocure 1173), 1-hydrorxycyclohexyl phenyl ketone, 2,2-dimethoxy-1,2-diphenylethan-1-one (Irgacure 651), 1-hydroxycyclohexyl phenyl ketone (Irgacure 184), Irgacure 127, Irgacure 500 (a mixture of Irgacure 184 and benzophenone), Irgacure 2959, Irgacure 907, Irgacure 369, Irgacure 379, Irgacure 754, Irgacure 1300, Irgacure 819, Irgacure 1700, Irgacure 1800, Irgacure 1850, Irgacure 1870, Darocure 4265, Darocure MBF, Darocure TPO, Irgacure 784, Irgacure 754, Irgacure OXE01, Irgacure OXE02. “Darocure” and “Irgacure” are trade names of the products available from Ciba Japan Co., Ltd. A known sensitizer may be added thereto, examples of which include isopropylthioxanthone, diethylthioxanthone, ethyl-4-dimethylaminobenzoate (Darocure EDB) and 2-ethylhexyl-4-dimethylaminobenzoate (Darocure EHA).

Examples of the photoradical polymerization initiator also include p-methoxyphenyl-2,4-bis(trichloromethyl)triazine, 2-(p-butoxystyryl)-5-trichloromethyl-1,3,4-oxadiazole, 9-phenylacridine, 9,10-benzphenazine, a mixture of benzophenone and Michler's ketone, a mixture of hexaarylbiimidazole and mercaptobenzimidazole, 1-(4-isopropylphenyl)-2-hydroxy-2-methylpropan-1-one, benzyldimethylketal, 2-methyl-1-(4-(methylthio)phenyl)-2-morpholinopropan-1-one, a mixture of 2,4-diethylxanthone and methyl p-dimethylaminobenzoate, and a mixture of benzophenone and methyltriethanolamine.

One or plural chain transfer agents may be added to the polymerizable liquid crystal composition to control the mechanical characteristics of the polymer. The use of a chain transfer agent enables to control the length of the polymer chain or the distance between two crosslinked polymer chains in the polymer film. These lengths can be controlled simultaneously. Increase of the amount of the chain transfer agent decreases the length of the polymer chain. Preferred examples of the chain transfer agent include a thiol compound. Examples of a monofunctional thiol compound include dodecanethiol and 2-ethylhexyl-(3-mercaptopropyonate). Examples of a polyfunctional thiol compound include trimethylolpropane tris(3-mercaptopropyonate), pentaerythritol tetrakis(3-mercaptopropyonate), 1,4-bis(3-mercaptobutyryloxy)butane (Karenz MT BD1), pentaerythritol tetrakis(3-mercaptobutyrate) (Karenz MT PE1), and 1,3,5-tris(3-mercaptobutyloxyethyl)-1,3,5-triazine-2,4,6(1H,3H,5H)-trione (Karenz MT NR1). “Karenz” is a trade name of the products available from Showa Denko Co., Ltd.

A polymerization inhibitor may be added to the polymerizable liquid crystal composition for preventing initiation of polymerization upon storing. A known polymerization inhibitor may be used, and preferred examples thereof include 2,5-di(t-butyl)hydroxytoluene (BHT), hydroquinone, Methylene Blue, diphenylpicric acid hydrazide (DPPH), benzothiadine, 4-nitrosodimethylaniline (NIDI) and o-hydroxybenzophenone.

An oxygen inhibitor may be added to the polymerizable liquid crystal composition for improving the storage stability thereof. A radical formed in the composition reacts with oxygen in the atmosphere to provide a peroxide radical, which accelerates unfavorable reaction with the polymerizable compound. An oxygen inhibitor is preferably added to prevent the phenomenon. Examples of the oxygen inhibitor include a phosphate ester compound.

In order to improve the weather resistance of the polymerizable liquid crystal composition, an ultraviolet ray absorbent, a light stabilizer (radical scavenger) and an antioxidant may be added. Examples of the ultraviolet ray absorbent include Tinuvin PS, Tinuvin P, Tinuvin 99-2, Tinuvin 109, Tinuvin 213, Tinuvin 234, Tinuvin 326, Tinuvin 328, Tinuvin 329, Tinuvin 384-2, Tinuvin 571, Tinuvin 900, Tinuvin 928, Tinuvin 1130, Tinuvin 400, Tinuvin 405, Tinuvin 460, Tinuvin 479, Tinuvin 5236, ADK STAB LA-32, ADK STAB LA-34, ADK STAB LA-36, ADK STAB LA-31, ADK STAB 1413 and ADK STAB LA-51. “Tinuvin” is a trade name of the products available from Ciba Japan Co., Ltd., and “ADK STAB” is a trade name of the products available from ADEKA Corporation.

Examples of the light stabilizer include Tinuvin 111FDL, Tinuvin 123, Tinuvin 144, Tinuvin 152, Tinuvin 292, Tinuvin 622, Tinuvin 770, Tinuvin 765, Tinuvin 780, Tinuvin 905, Tinuvin 5100, Tinuvin 5050, Tinuvin 5060, Tinuvin 5151, Chimassorb 119FL, Chimassorb 944FL, Chimassorb 944LD, ADK STAB LA-52, ADK STAB LA-57, ADK STAB LA-62, ADK STAB LA-67, ADK STAB LA-63P, ADK STAB LA-68LD, ADK STAB LA-77, ADK STAB LA-82, ADK STAB LA-87, Cyasorb UV-3346, available from Nihon Cytec Industries Inc., and Good-rite UV-3034, available from Goodrich Corp. “Chimassorb” is a trade name of a commercial product available from Ciba Japan Co., Ltd.

Examples of the antioxidant include ADK STAB AO-20, AO-30, AO-40, AO-50, AO-60 and AO-80, available from Asahi Denka Co., Ltd., Sumilizer BHT, Sumilizer BBM-S and Sumilizer GA-80, available from Sumitomo Chemical Co., Ltd., and Irganox 1076, Irganox 1010, Irganox 3114 and Irganox 245, available from Ciba Japan Co., Ltd. These commercially available products may be used in the invention.

A silane coupling agent other than the compound (5) may be added to the polymerizable liquid crystal composition for controlling adhesion to the substrate. Specific examples of the silane coupling agent include vinyltrialkoxysilane, 3-isocyanatepropyltrialkoxysilane, N-(2-aminoethyl)-3-aminopropyltrialkoxysilane, 3-glycidoxypropyltrialkoxysilane, 3-chlorotrialkoxysilane, 3-acryloxypropyltrimethoxysilane and 3-methacryloxypropyltrialkoxysilane. Examples thereof also include dialkoxymethylsilane compounds obtained by replacing one of the three alkoxy groups of these compounds by methyl.

The polymerizable liquid crystal composition may be coated as it is on the surface of the substrate. However, in general, for facilitating the coating operation, the polymerizable liquid crystal composition is diluted with a solvent, or in alternative, the components of the polymerizable liquid crystal composition are each dissolved in a solvent, thereby preparing a solution of the polymerizable liquid crystal composition containing the polymerizable liquid crystal composition and the solvent, and the solution is coated. A solvent may be used solely or as a mixture of two or more thereof. Examples of the solvent include an ester, an amide, an alcohol, an ether, a glycol monoalkyl ether, an aromatic hydrocarbon, a halogenated aromatic hydrocarbon, an aliphatic hydrocarbon, a halogenated aliphatic hydrocarbon, an alicyclic hydrocarbon and a ketone.

Preferred examples of the ester include alkyl acetate (such as methyl acetate, ethyl acetate, propyl acetate, isopropyl acetate, butyl acetate, 3-methoxybutyl acetate, isobutyl acetate, pentyl acetate, isopentyl acetate, methyl acetoacetate, α-terpinyl acetate, perillyl acetate, 3-octyl acetate, 2-octyl acetate, myrtenyl acetate, isobornyl acetate, dihydroterpinyl acetate, dihydrocarbyl acetate, carbyl acetate and 1-methoxy-2-propyl acetate), ethyl trifluoroacetate, alkyl propionate (such as methyl propionate, methyl 3-methoxypropyonate, ethyl propionate, propyl propionate and butyl propionate), alkyl butyrate (such as methyl butyrate, ethyl butyrate, butyl butyrate, isobutyl butyrate and propyl butyrate), dialkyl malonate (such as diethyl malonate), alkyl glycolate (such as methyl glycolate and ethyl glycolate), alkyl lactate (such as methyl lactate, ethyl lactate, isopropyl lactate, n-propyl lactate, butyl lactate and ethylhexyl lactate), monoacetin, γ-butyrolactone and γ-valerolactone.

Preferred examples of the amide include N-methyl-2-pyrrolidone, N,N-diemthylacetamide, N-methylpropyonamide, N,N-dimethylormamide, N,N-diethylformamide, N,N-diethylacetamide, N,N-diemthylacetamide dimethylacetal, N-methylcaprolactam and dimethylimidazolidinone.

Preferred examples of the alcohol include methanol, ethanol, 1-propanol, 2-propanol, 1-methoxy-2-propanol, t-butyl alcohol, sec-butyl alcohol, butanol, 2-ethylbutanol, n-hexanol, n-heptanol, n-octanol, 1-dodecanol, ethylhexanol, 3,5,5-trimethylhexanol, n-amyl alcohol, hexafluoro-2-propanol, glycerin, ethylene glycol, diethylene glycol, triethylene glycol, tetraethylene glycol, propylene glycol, dipropylene glycol, tripropylene glycol, hexylene glycol, 1,3-butanediol, 1,4-butanediol, 2,3-butanediol, 1,5-pentanediol, 2,4-pentanediol, 2,5-hexanediol, 3-methyl-3-methoxybutanol, cyclohexanol and methylcyclohexanol.

Preferred examples of the ether include ethylene glycol dimethyl ether, diethylene glycol dimethyl ether, bis(2-propyl)ether, 1,4-dioxane, cyclopentyl methyl ether, terpinyl methyl ether, dihydroterpinyl methyl ether, 1,8-cineole, 1,4-cineole and tetrahydrofuran (THF).

Preferred examples of the glycol monoalkyl ether include ethylene glycol monoalkyl ether (such as ethylene glycol monomethyl ether and ethylene glycol monobutyl ether), diethylene glycol monoalkyl ether (such as diethylene glycol monoethyl ether), triethylene glycol monoalkyl ether, propylene glycol monoalkyl ether (such as propylene glycol monobutyl ether), dipropylene glycol monoalkyl ether (such as dipropylene glycol monomethyl ether), ethylene glycol monoalkyl ether acetate (such as ethylene glycol monobutyl ether acetate), diethylene glycol monoalkyl ether acetate (such as diethylene glycol monoethyl ether acetate), triethylene glycol monoalkyl ether acetate, propylene glycol monoalkyl ether acetate (such as propylene glycol monomethyl ether acetate, propylene glycol monoethyl ether acetate and propylene glycol monobutyl ether acetate), dipropylene glycol monoalkyl ether acetate (such as dipropylene glycol monomethyl ether acetate), and diethylene glycol methyl ethyl ether.

Preferred examples of the aromatic hydrocarbon include benzene, toluene, xylene, mesitylene, ethylbenzene, diethylbenzene, i-propylbenzene, n-propylbenzene, tert-butylbenzene, sec-butylbenzene, n-butylbenzene, anisole, p-cymene, limonene, terpinolene and tetralin. Preferred examples of the halogenated aromatic hydrocarbon solvent include chlorobenzene.

Preferred examples of the aliphatic hydrocarbon include hexane and heptane. Preferred examples of the halogenated aliphatic hydrocarbon include chloroform, dichloromethane, carbon tetrachloride, dichloroethane, trichloroethylene and tetrachloroethylene. Preferred examples of the alicyclic hydrocarbon include cyclohexane and decalin.

Preferred examples of the ketone include acetone, methyl ethyl ketone, methyl isobutyl ketone, cyclohexanone, cyclopentanone, dihydrocarvone, menthone, piperitenone and methyl propyl ketone.

An amide, an aromatic hydrocarbon and a ketone are preferably used from the standpoint of solubility of the polymerizable liquid crystal compounds, and an ester, an alcohol, an ether and a glycol monoalkyl ether are also preferably used in combination therewith from the standpoint of the boiling point of the solvent. There is no particular limitation on selecting the solvent. In the case where a plastic substrate is used as the supporting substrate, it is necessary to lower the drying temperature to prevent the substrate from being deformed, and is also necessary to prevent the substrate from being damaged with the solvent. Preferred examples of the solvent used in this case include an aromatic hydrocarbon, a ketone, an ester, an ether, an alcohol and a glycol monoalkyl acetate.

The ratio of the solvent in the solution of the polymerizable liquid crystal composition is generally from 50 to 95% based on the total weight of the solution. The lower limit is determined in consideration of the solubility of the polymerizable liquid crystal compounds and the optimum viscosity upon coating the solution. The upper limit is determined in consideration of the economical issues, such as the cost for the solvent and the time and amount of heat necessary for evaporating the solvent. The ratio of the solvent is preferably from 60 to 90%, and more preferably from 70 to 85%.

In the following description, a liquid crystal film of the invention obtained from the polymerizable liquid crystal composition may be referred simply to as a liquid crystal film in some cases. The liquid crystal film can be produced in the following manner. The solution of the polymerizable liquid crystal composition is coated on a supporting substrate, and then dried to form a coated film. The coated film is then irradiated with light to polymerize the polymerizable liquid crystal composition, thereby fixing the nematic alignment formed by the composition in a liquid crystal state in the coated film. Examples of the supporting substrate that can be used herein include glass and a plastic film. Examples of the plastic film include films of polyimide, polyamideimide, polyamide, polyetherimide, polyetheretherketone, polyetherketone, polyketone sulfide, polyether sulfone, polysulfone, polyphenylene sulfide, polyphenylene oxide, polyethylene terephthalate, polybutylene terephthalate, polyethylene naphthalate, polyacetal, polycarbonate, polyarylate, an acrylic resin, polyvinyl alcohol, polypropylene, cellulose, triacetyl cellulose, a partially saponified product of triacetyl cellulose, an epoxy resin, a phenol resin and a cycloolefin resin.

Examples of the cycloolefin resin include a norbornene resin and a dicyclopentadiene resin, but the invention is not limited thereto. Among these, those having no unsaturated bond or having unsaturated bonds that have been hydrogenated are preferably used. Examples thereof include a hydrogenated product of a ring-opening (co)polymer of one or plural kinds of norbornene monomers, an addition (co)polymer of one or plural kinds of norbornene monomers, an addition copolymer of a norbornene monomer and an olefin monomer (such as ethylene and an α-olefin), an addition copolymer of a norbornene monomer and a cycloolefin monomer (such as cyclopentene, cyclooctene and 5,6-dihyroxycyclopentadiene), and modified products thereof. Specific examples thereof include Zeonex and Zeonor (available from Nippon Zeon Corp.), Arton (available from JSR Corporation), TOPAS (available from Ticona, Inc.), Apel (available from Mitsui Chemicals, Inc.), Escena (available from Sekisui Chemical Co., Ltd.) and Optorez (available from Hitachi Chemical Co., Ltd.).

The plastic film may be a uniaxially stretched film or a biaxially stretched film. The plastic film may be subjected to a surface treatment, such as a hydrophilic treatment, e.g., a corona treatment and a plasma treatment, and a hydrophobic treatment. While the method for the hydrophilic treatment is not particularly limited, a corona treatment and a plasma treatment are preferred, and a plasma treatment is particularly preferred. The plasma treatment can be effected by a method disclosed, for example, in JP-2002-226616-A and JP-2002-121648-A. An anchor coating layer may be formed for improving adhesion between the liquid crystal film and the plastic film. The anchor coating layer may be formed of an inorganic material or an organic material as far as the layer improves adhesion between the liquid crystal film and the plastic film. The plastic film may be a laminated film. Instead of the plastic film, a metallic substrate, such as aluminum, iron and copper, having slit grooves formed on the surface thereof, and a glass substrate, such as alkali glass, borosilicate glass and flint glass, having been etched to form grooves in a slit form may also be used.

The supporting substrate, such as the glass substrate and the plastic film, may be subjected to a physical or mechanical surface treatment, such as rubbing, before forming a coated film of the polymerizable liquid crystal composition. Although a surface treatment, such as a rubbing treatment, is often not carried out upon forming a polymerizable liquid crystal layer and a liquid crystal film that have a homeotropic alignment, a rubbing treatment may be carried out for preventing alignment defects and the like from occurring. The rubbing treatment may be carried out by the following methods. A rubbing cloth formed of a material such as rayon, cotton or polyamide is wound on a metallic roll, and the roll is rotated and moved in a state where the roll is in contact with the supporting substrate or the polymer film, or the supporting substrate is moved with the rotated roll staying. The rubbing treatment may be carried out directly on the supporting substrate, or on the polymer film that is formed on the supporting substrate in advance. Depending on the species of the supporting substrate, silicon oxide may be deposited on the surface thereof by oblique vapor deposition to impart alignment capability.

Examples of a coating method for obtaining a coated film having a uniform thickness upon coating the polymerizable liquid crystal composition or a solution thereof include a spin coating method, a microgravure coating method, a gravure coating method, a wire bar coating method, a dip coating method, a spray coating method, a meniscus coating method and a die coating method. In particular, a wire bar coating method and the like, in which a shearing force is applied to the liquid crystal composition upon coating, may be employed in the case where the alignment of the liquid crystal composition is controlled without a surface treatment, such as rubbing, on the substrate.

Upon preparing the solution of the polymerizable liquid crystal composition, the compound (5) may be used after dissolving with a solvent in advance. The solvent is selected from such solvents that have sufficient solubility with the compound (5) and do not impair the stability and uniformity of the homeotropic alignment state of the polymerizable liquid crystal composition, which are advantages of the invention. Examples of the solvent include those solvents that have been described for preparation of the solution of the polymerizable liquid crystal composition. The amount of the solvent used may be set within such a range that the stability of the polymerizable liquid crystal composition is not impaired.

Upon coating the solution of the polymerizable liquid crystal composition of the invention, the solvent is removed after coating to form a polymerizable liquid crystal layer, i.e., a layer of the polymerizable liquid crystal composition, having a uniform thickness on the supporting substrate. The conditions for removing the solvent are not particularly limited, and the coated film may be dried to such an extent that the solvent has been substantially removed, and the coated film of the polymerizable liquid crystal composition loses flowability. The solvent can be removed by air drying at room temperature, drying with a hot plate, drying in a drying furnace, blowing warm air or hot air, or the like. The polymerizable liquid crystal composition in the coated film may complete a nematic alignment during the drying operation of the coated film in some cases, depending on the kinds and the compositional ratios of the compounds used in the polymerizable liquid crystal composition. In this case, accordingly, the coated film after completing the drying step can be subjected to a polymerizing step without subjecting to a heat-treating step described later.

Preferred ranges of the conditions, such as the temperature and time for the heat treatment of the coated film, the wavelength of light used for light irradiation, the amount of light radiated from a light source, vary depending on the kinds and compositional ratios of the compounds used in the polymerizable liquid crystal composition, the presence or absence and the addition amount of the photopolymerization initiator, and the like. Accordingly, the conditions including the temperature and time for the heat treatment of the coated film, the wavelength of light used for light irradiation, and the amount of light radiated from a light source described later are considered to be approximate ranges.

The heat treatment of the coated film is preferably carried out under such conditions that the solvent is removed, and a homogeneous alignment of the polymerizable liquid crystal is obtained. The heat treatment may be carried out at a temperature higher than the liquid crystal phase transition temperature of the polymerizable liquid crystal composition. One example of the heat-treating method is a method of heating the coated film to a temperature where the polymerizable liquid crystal composition exhibits a nematic liquid crystal phase, whereby the polymerizable liquid crystal composition in the coated film forms a nematic alignment. A nematic alignment may be formed by changing the temperature of the coated film within a temperature range where the polymerizable liquid crystal composition exhibits a nematic liquid crystal phase. In this method, the coated film is heated to a high temperature region within the aforementioned temperature range to complete substantially a nematic alignment of the coated film, and then the temperature is decreased to make an alignment with higher regularity. In both cases using the heat-treating methods, the heat-treating temperature may be from room temperature to 120° C., preferably from room temperature to 100° C., more preferably from room temperature to 90° C., and further preferably from room temperature to 85° C. The heat-treating time is generally from 5 seconds to 2 hours, preferably from 10 seconds to 40 minutes, and more preferably from 20 seconds to 20 minutes. In order to increase the temperature of the layer containing the polymerizable liquid crystal composition to the prescribed temperature, the heat-treating time is preferably 5 seconds or more. In order to prevent the productivity from being deteriorated, the heat-treating time is preferably 2 hours or less. The polymerizable liquid crystal layer of the invention is thus completed in this manner.

The nematic alignment state of the polymerizable liquid crystal compounds formed in the polymerizable liquid crystal layer is fixed by polymerizing the polymerizable liquid crystal composition through irradiation of light. The wavelength of the light used for the light irradiation is not particularly limited, and an electron beam, an ultraviolet ray, a visible ray, an infrared ray (heat ray) and the like may be used. In general, an ultraviolet ray or a visible ray may be used. The wavelength is generally in a range of from 150 to 500 nm, preferably in a range of from 250 to 450 nm, and more preferably in a range of from 300 to 400 nm. Examples of the light source include a low pressure mercury lamp (such as a bactericidal lamp, a fluorescent chemical lamp and a black light lamp), a high pressure discharge lamp (such as a high pressure mercury lamp and a metal halide lamp), and a short arc discharge lamp (such as a super high pressure mercury lamp, a xenon lamp and a mercury xenon lamp). Preferred examples of the light source include a metal halide lamp, a xenon lamp, a super high pressure mercury lamp and a high pressure mercury lamp. The wavelength range of the light source used for irradiation may be selected by inserting a filter between the light source and the polymerizable liquid crystal layer to pass the specific wavelength range. The amount of light radiated from the light source is generally from 2 to 5,000 mJ/cm², preferably from 10 to 3,000 mJ/cm², and more preferably from 100 to 2,000 mJ/cm². The temperature condition upon irradiation of light is preferably set similarly to the heat-treating temperature. The atmosphere upon polymerization may be any of a nitrogen atmosphere, an inert gas atmosphere and an air atmosphere, and a nitrogen atmosphere and an inert gas atmosphere are preferred from the standpoint of enhancement of the curing property.

In the case where the polymerizable liquid crystal layer of the invention and a liquid crystal film obtained by polymerizing it through light or heat are used in various optical devices, and in the case where they are used as an optical compensation device used in a liquid crystal display device, it is considerably important to control the distribution of the tilt angle thereof in the thickness direction.

Examples of the method for controlling the tilt angle include a method of controlling the kinds and the compositional ratios of the liquid crystal compounds used in the polymerizable liquid crystal composition. The tilt angle may also be controlled by adding other components to the polymerizable liquid crystal composition. The tilt angle of the liquid crystal film can also be controlled by the kind of the solvent and the concentration of the solute in the polymerizable liquid crystal composition. In the invention, a surfactant may be used for facilitating the coating operation on the supporting substrate, and the kind and the amount of the surfactant added are carefully selected to prevent the homeotropic alignment as an advantage of the invention from being impaired since they influence the tilt angle. The tilt angle of the liquid crystal film can be controlled by the kind and the rubbing condition of the supporting substrate and the polymer film, the drying condition and the heat treatment condition for the coated film of the polymerizable liquid crystal composition, and the like. The irradiation atmosphere in the photopolymerization step after alignment and the temperature upon irradiation also influence the tilt angle of the liquid crystal film. In other words, it can be considered that substantially all the conditions in the production process of the liquid crystal film influence the tilt angle in any way. Accordingly, a tilt angle suitable for a target product can be provided by appropriately selecting the conditions in the production process of the liquid crystal film, in addition to optimization of the polymerizable liquid crystal composition.

In a homeotropic alignment, the tilt angle is uniformly distributed from 85 to 90° over the substrate interface to the free interface. This alignment state is obtained by forming on a surface of a supporting substrate a coated film of the polymerizable liquid crystal composition of the invention containing the mixture of polymerizable compounds containing the components A to D, and the component E. For providing a uniform homeotropic alignment in the invention, it is preferred to use the component A in a ratio of from 10 to 55% by weight, the component B in a ratio of from 3 to 20% by weight, the component C in a ratio of from 10 to 50% by weight and the component D in a ratio of from 10 to 77% by weight, in the mixture of polymerizable compounds as described above.

The component A is at least one compound selected from the compound (1-1), and preferred examples of the compound (1-1) include the compounds (1-1-A1) and (1-1-A2).

The component B is at least one compound selected from the compound (2-1) or at least one compound selected from the compounds (2-2) to (2-4). Preferred examples of the compound (2-1) include the compounds (2-1-D1), (2-1-D2), (2-1-G1) and (2-1-G2). Preferred examples of the compounds (2-2) to (2-4) include the compounds (2-2-A1), (2-3-A1) and (2-4-A1).

The component C is at least one compound selected from the compound (3-1), and preferred examples of the compound (3-1) include the compounds (3-1-A1) to (3-1-A4) and (3-1-G1) to (3-1-G8).

The component D is at least one compound selected from the compound (4), and preferred examples of the compound (4) include the compounds (4-1-A1) to (4-1-A4), (4-1-G1) and (4-1-G2).

The ratio of the component E is preferably from 0.01 to 0.20 in terms of weight ratio based on the total weight of the components A to D as described above. The component E is at least one compound selected from the compound (5), and preferred examples of the compound (5) include the compounds (5-1-1) to (5-1-3).

For forming a uniform homeotropic alignment, plural kinds of the compounds (2) as the component B may be used in combination. The compound (2) may be added to the polymerizable liquid crystal composition directly or after diluting with a solvent or the like. There are cases where a uniform homeotropic alignment is difficult to be formed by the aforementioned method depending on the kind of the polymerizable liquid crystal compound and the formulation of the polymerizable liquid crystal composition. In these cases, it is considered that the homogeneous alignment property of the tilted alignment property is strong, and thus the addition amount of the component C or the component E is increased, or the amount of the component D is decreased to the minimum necessary value, thereby providing a uniform homeotropic alignment. In the case where the surface of the supporting substrate has polarity through a hydrophilic treatment or the like, a more uniform homeotropic alignment can be obtained without a surface treatment, such as a rubbing treatment.

For controlling the birefringence, a polymerizable liquid crystal layer having a low birefringence value can be obtained by increasing the ratio of the component A used, and a polymerizable liquid crystal layer having a high birefringence value can be obtained by decreasing the ratio of the component A used.

In the case where a vertical alignment agent is formed on the supporting substrate, lecithin, a chromium complex, a polyimide alignment film for vertical alignment, a low-temperature (less than 180° C.) baked film of a polyamic acid alignment film, a high-temperature (180° C. or more) baked film of a polyamic acid alignment film, a water-soluble silsesquioxane film or a side-chain type liquid crystal polymer may be coated on the supporting substrate.

A suitable thickness of the liquid crystal film varies depending on the retardation and the birefringence of the liquid crystal film corresponding to the target device. Therefore, the suitable range thereof cannot be determined strictly and may be generally from 0.05 to 50 μm, preferably from 0.1 to 20 μm, and more preferably from 0.5 to 10 μm. The liquid crystal film preferably has a haze of 1.5% or less, and more preferably 1.0% or less, and a transmittance of 80% or more, and more preferably 95% or more. The conditions of transmittance are preferably satisfied in the visible ray region.

The liquid crystal film can be effectively utilized as an optical compensation device applied to a liquid crystal display device (particularly, a liquid crystal display device of an active matrix type or a passive matrix type). Examples of the type of the liquid crystal display device, to which the anisotropic polymer is suitably applied as an optical compensation film, include an IPS (in-plane switching) type, a display having switch in an optically isotropic phase (described, for example, in WO 02/93244), a TN (twisted nematic) type, an STN (super twisted nematic) type, an ECB (electrically controlled birefringence) type, a DAP (deformation of aligned phases) type, a CSH (color super homeotropic) type, a VA (vertical alignment) type, a VAN/VAC (vertically aligned nematic/cholesteric) type, an MVA (multi-domain vertical alignment) type, a PVA (patterned vertical alignment) type, an OCB (optically compensated birefringence) type, an R-OCB (reflective optically compensated birefringence) type, an HAN (hybrid aligned nematic) type, an OMI (optical mode interference) type and SBE (super birefringence effect) type. Furthermore, the liquid crystal film can be used as a phase retarder for a display device of a guest-host type, a ferroelectric type, antiferroelectric type or the like. Preferred examples of the type of the liquid crystal display device include a TN type, an STN type, a VA type and an IPS type, and particularly an active matrix type display. The optimum values of the parameters demanded for the anisotropic polymer, such as the distribution of tilt angle in the thickness direction and the thickness, strongly depend on the kind and the optical parameters of the liquid crystal display device that is to be compensated, and thus vary depending on the kind of the device.

The liquid crystal film can be used as an optical device having a polarizing plate and the like integrated therewith, and in this case, the liquid crystal film is disposed outside the liquid crystal cell. The liquid crystal film as an optical compensation device can be disposed inside the liquid crystal cell since it suffers no or less elution of impurities into the liquid crystal charged in the cell. For example, by applying the techniques disclosed in JP-2008-01943-A, the polymerizable liquid crystal layer of the invention can be formed on a color filter to enhance the function of the color filter.

EXAMPLES

The invention will be described in more detail below with reference to Examples, but the invention is not construed as being limited to the examples. Evaluation methods used in the Examples are shown below. The term “polymerizable liquid crystal composition” in the Examples means the solution of the polymerizable liquid crystal composition.

<Polymerization Conditions>

A polymerizable composition was irradiated with light having an intensity of 30 mW/cm² (365 nm) by using a 250 W super high pressure mercury lamp at room temperature under a nitrogen atmosphere or air for 30 seconds.

<Confirmation of Alignment State of Liquid Crystal>

A resulting substrate having a liquid crystal film was held between two polarizing plates, which were disposed to form crossed nicols. In the case where it was confirmed that a dark field was observed when the substrate was viewed from the front, and a bright field was observed when the substrate was viewed from the left, right, top and bottom directions, the case indicated that the alignment vector of the liquid crystal skeleton was perpendicular to the glass substrate, and thus it was determined that a homeotropic alignment was formed. The uniformity of the homeotropic alignment was confirmed in the following manner. The substrate having a liquid crystal film was held between two polarizing plates, which were disposed to form crossed nicols, and was observed from the front. When leakage of light due to alignment defects of the liquid crystal was not observed visually (dark field), it was determined that a uniform alignment was formed. The supporting substrate used was non-alkali glass, or slide glass having coated and baked thereon polyamic acid having no long-chain alkali. The polymerizable liquid crystal composition was coated and aligned on the supporting substrate, and polymerized under the aforementioned polymerization conditions.

<Measurement with Ellipsometer>

The polymer film was irradiated with light having a wavelength of 550 nm with Optipro Ellipsometer, available from Shintech Co., Ltd. The retardation was measured by decreasing the incident angle of the light with respect to the film surface from 90°. The retardation is expressed by Δn×d, wherein Δn represents the optical anisotropy, and d represents the thickness of the polymer film.

The compounds used in the Examples are shown below.

The compound (1-1-A2) was synthesized according to the method disclosed in JP-2006-111571-A.

The compound (2-1-D2) was synthesized according to the method disclosed in JP-2007-16213-A.

The compound (2-1-G2) was synthesized according to the method disclosed in JP-2008-133344-A.

The compound (2-2-A1) used was Ogsol CA-0400, the compound (2-3-A1) used was Ogsol EA-0200 (m23+n23=2) or Ogsol EA-0500 (m23+n23=5), and the compound (2-4-A1) used was ONF-1. These were commercially available products of Osaka Gas Chemicals Co., Ltd.

The compound (3-1-A2) was synthesized according to the method disclosed in Macromolecules, vol. 26, pp. 6132-6134 (1993).

The compound (3-1-G2) was synthesized according to the method disclosed in JP-2005-187618-A.

The compounds (4-1-A1) and (4-1-A3) were synthesized according to the method disclosed in JP-2003-238491-A.

The compound (4-1-G1) was synthesized according to the method disclosed in U.S. Pat. No. 5,770,107.

Example 1

The compounds (1-1-A2), (2-1-D2), (3-1-A2) and (4-1-A3) were mixed at a ratio (1-1-A2)/(2-1-D2)/(3-1-A2)/(4-1-A3)=40/10/25/25 by weight. The resulting mixture was designated as MIX 1. The compound (5-1-1) (SILA-ACE S-330, a trade name, available from Chisso Corporation) in a weight ratio of 0.10 and a polymerization initiator (Irgacure 907, a trade name, available from Ciba Japan Co., Ltd.) in a weight ratio of 0.03 were added to MIX 1. A mixed solvent of toluene and 2-propanol (toluene/2-propanol=9/1 by weight) was added to the resulting composition to prepare a polymerizable liquid crystal composition (1) having a solvent ratio of 70% by weight.

An alignment agent for low pre-tilt angle (horizontal alignment mode) (Lixon Aligner PIA-5310, a trade name, available from Chisso Corporation) was coated on a glass substrate (S-1112, available from Matsunami Glass Industries, Ltd.), and after drying at 80° C. for 3 minutes, the coated film was baked at 210° C. for 30 minutes. The polymerizable liquid crystal composition (1) was coated by a spin coating method on the glass substrate having been subjected to the alignment treatment. The substrate was heated to 70° C. for 3 minutes and cooled at room temperature for 3 minutes, and the coated film, from which the solvent was removed, was polymerized with an ultraviolet ray under a nitrogen stream to provide a liquid crystal film having a uniform homeotropic alignment. The measurement of the retardation of the film provided the results shown in FIG. 1.

Example 2

A liquid crystal film was formed in the same manner as in Example 1 except that a glass substrate was used as the supporting substrate, and a liquid crystal film having a uniform homeotropic alignment. The measurement of the retardation of the film provided results similar to FIG. 1.

Example 3

The compounds (1-1-A2), (2-4-A1), (3-1-A2) and (4-1-A3) were mixed at a ratio (1-1-A2)/(2-4-A1)/(3-1-A2)/(4-1-A3)=40/10/25/25 by weight. The resulting mixture was designated as MIX 2. The compound (5-1-1) in a weight ratio of 0.10 and a polymerization initiator (Irgacure 907) in a weight ratio of 0.06 were added to MIX 2. A mixed solvent of methyl 3-methoxypropionate and propylene glycol monomethyl ether acetate (methyl 3-methoxypropionate/propylene glycol monomethyl ether acetate=1/1 by weight) was added to the resulting composition to prepare a polymerizable liquid crystal composition (2) having a solvent ratio of 80% by weight. A liquid crystal film having a uniform homeotropic alignment was obtained in the same manner as in Example 1 except that the polymerizable liquid crystal composition (2) was used and polymerized under air. The measurement of the retardation of the film provided results similar to FIG. 1.

Example 4

The compounds (1-1-A2), (2-1-G2), (3-1-A2) and (4-1-A3) were mixed at a ratio (1-1-A2)/(2-1-G2)/(3-1-A2)/(4-1-A3)=40/10/25/25 by weight. The resulting mixture was designated as MIX 3. A polymerizable liquid crystal composition (3) was prepared in the same manner as in Example 3 except that MIX 3 was used. A liquid crystal film having a uniform homeotropic alignment was obtained in the same manner as in Example 3 except that the polymerizable liquid crystal composition (3) was used, and a glass substrate was used as the supporting substrate. The measurement of the retardation of the film provided results similar to FIG. 1.

Example 5

The compounds (1-1-A2), (2-3-A1) (m23+n23=5), (3-1-A2) and (4-1-A3) were mixed at a ratio (1-1-A2)/(2-3-A1)/(3-1-A2)/(4-1-A3)=40/10/25/25 by weight. The resulting mixture was designated as MIX 4. A polymerizable liquid crystal composition (4) was prepared in the same manner as in Example 3 except that MIX 4 was used. A liquid crystal film having a uniform homeotropic alignment was obtained in the same manner as in Example 3 except that the polymerizable liquid crystal composition (4) was used. The measurement of the retardation of the film provided results similar to FIG. 1.

Example 6

The compounds (1-1-A2), (2-3-A1) (m23+n23=5), (3-1-A2) and (4-1-A3) were mixed at a ratio (1-1-A2)/(2-3-A1)/(3-1-A2)/(4-1-A3)=30/10/35/25 by weight. The resulting mixture was designated as MIX 5. A polymerizable liquid crystal composition (5) was prepared in the same manner as in Example 3 except that MIX 5 was used. A liquid crystal film having a uniform homeotropic alignment was obtained in the same manner as in Example 3 except that the polymerizable liquid crystal composition (5) was used. The measurement of the retardation of the film provided results similar to FIG. 1.

Example 7

The compounds (1-1-A2), (2-3-A1) (m23+n23=2), (3-1-A2) and (4-1-A3) were mixed at a ratio (1-1-A2)/(2-3-A1)/(3-1-A2)/(4-1-A3)=25/10/35/30 by weight. The resulting mixture was designated as MIX 6. A polymerizable liquid crystal composition (6) was prepared in the same manner as in Example 3 except that MIX 6 was used. A liquid crystal film having a uniform homeotropic alignment was obtained in the same manner as in Example 3 except that the polymerizable liquid crystal composition (6) was used. The measurement of the retardation of the film provided results similar to FIG. 1.

Example 8

The compounds (1-1-A2), (2-2-A1), (3-1-A2) and (4-1-A3) were mixed at a ratio (1-1-A2)/(2-2-A1)/(3-1-A2)/(4-1-A3)=25/10/35/30 by weight. The resulting mixture was designated as MIX 7. A polymerizable liquid crystal composition (7) was prepared in the same manner as in Example 3 except that MIX 7 was used. A liquid crystal film having a uniform homeotropic alignment was obtained in the same manner as in Example 3 except that the polymerizable liquid crystal composition (7) was used. The measurement of the retardation of the film provided results similar to FIG. 1.

Example 9

The compounds (1-1-A2), (2-3-A1) (m23+n23=2), (3-1-A2), (4-1-A3) and (4-1-G1) were mixed at a ratio (1-1-A2)/(2-3-A1)/(3-1-A2)/(4-1-A3)/(4-1-G1)=25/10/35/25/5 by weight. The resulting mixture was designated as MIX 8. A polymerizable liquid crystal composition (8) was prepared in the same manner as in Example 3 except that MIX 8 was used, and a mixed solvent of toluene and 2-propanol (toluene/2-propanol=9/1 by weight) was used as the solvent. A liquid crystal film having a uniform homeotropic alignment was obtained in the same manner as in Example 3 except that the polymerizable liquid crystal composition (8) was used. The measurement of the retardation of the film provided results similar to FIG. 1.

Example 10

The compounds (1-1-A2), (2-3-A1) (m23+n23=2), (3-1-A2) and (4-1-A1) were mixed at a ratio (1-1-A2)/(2-3-A1)/(3-1-A2)/(4-1-A1)=25/10/35/30 by weight. The resulting mixture was designated as MIX 9. A polymerizable liquid crystal composition (9) was prepared in the same manner as in Example 3 except that MIX 9 was used. A liquid crystal film having a uniform homeotropic alignment was obtained in the same manner as in Example 3 except that the polymerizable liquid crystal composition (9) was used. The measurement of the retardation of the film provided results similar to FIG. 1.

Example 11

The compounds (1-1-A2), (2-3-A1) (m23+n23=2), (3-1-G2) and (4-1-A1) were mixed at a ratio (1-1-A2)/(2-3-A1)/(3-1-G2)/(4-1-A1)=25/10/35/30 by weight. The resulting mixture was designated as MIX 10. A polymerizable liquid crystal composition (10) was prepared in the same manner as in Example 3 except that MIX 10 was used, and a mixed solvent of toluene and 2-propanol (toluene/2-propanol=9/1 by weight) was used as the solvent. A liquid crystal film having a uniform homeotropic alignment was obtained in the same manner as in Example 3 except that the polymerizable liquid crystal composition (10) was used. The measurement of the retardation of the film provided results similar to FIG. 1.

Comparative Example 1

The compounds (1-1-A2), (3-1-A2) and (4-1-A3) were mixed at a ratio (1-1-A2)/(3-1-A2)/(4-1-A3)=30/35/35 by weight to prepare a mixture MIX-A, and a polymerizable liquid crystal composition (A) was prepared in the same manner as in Example 1 except that MIX-A was used, and the compound (5-1-1) was not added. A liquid crystal film was formed in the same manner as in Example 1 except that the polymerizable liquid crystal composition (A) was used, and the liquid crystal film exhibited a random alignment.

Comparative Example 2

A polymerizable liquid crystal composition (B) was prepared in the same manner as in Example 1 except that MIX-A in Comparative Example 1 was used, and the compound (5-1-1) in a weight ratio of 0.10 was added thereto. A liquid crystal film was formed in the same manner as in Example 1 except that the polymerizable liquid crystal composition (B) was used, and the liquid crystal film exhibited a random alignment.

Comparative Example 3

The compounds (1-1-A2), (2-1-D2), (3-1-A2) and (4-1-A3) were mixed at a ratio (1-1-A2)/(2-1-D2)/(3-1-A2)/(4-1-A3)=40/10/25/25 by weight to prepare a mixture MIX-B, and a polymerizable liquid crystal composition (C) was prepared in the same manner as in Example 1 except that MIX-B was used, and the compound (5-1-1) was not added. A liquid crystal film was formed in the same manner as in Example 1 except that the polymerizable liquid crystal composition (C) was used, and the liquid crystal film exhibited a random alignment.

Comparative Example 4

The compounds (1-1-A2), (2-4-A1), (3-1-A2) and (4-1-A3) were mixed at a ratio (1-1-A2)/(2-4-A1)/(3-1-A2)/(4-1-A3)=40/10/25/25 by weight to prepare a mixture MIX-C, and a polymerizable liquid crystal composition (D) was prepared in the same manner as in Example 3 except that MIX-C was used, and the compound (5-1-1) was not added. A liquid crystal film was formed in the same manner as in Example 3 except that the polymerizable liquid crystal composition (D) was used, and the liquid crystal film exhibited a random alignment.

Comparative Example 5

The compounds (1-1-A2), (2-1-G2), (3-1-A2) and (4-1-A3) were mixed at a ratio (1-1-A2)/(2-1-G2)/(3-1-A2)/(4-1-A3)=40/10/25/25 by weight to prepare a mixture MIX-D, and a polymerizable liquid crystal composition (E) was prepared in the same manner as in Example 4 except that MIX-D was used, and the compound (5-1-1) was not added. A liquid crystal film was formed in the same manner as in Example 3 except that the polymerizable liquid crystal composition (E) was used, and the liquid crystal film exhibited a random alignment.

Comparative Example 6

The compounds (1-1-A2), (3-1-A2), (4-1-A3) and (4-1-G1) were mixed at a ratio (1-1-A2)/(3-1-A2)/(4-1-A3)/(4-1-G1)=35/35/25/5 by weight to prepare a mixture MIX-E, and a polymerizable liquid crystal composition (F) was prepared in the same manner as in Example 9 except that MIX-E was used, and the compound (5-1-1) was not added. A liquid crystal film was formed in the same manner as in Example 3 except that the polymerizable liquid crystal composition (F) was used, and the liquid crystal film exhibited a random alignment.

Comparative Example 7

A polymerizable liquid crystal composition (G) was prepared in the same manner as in Example 9 except that MIX-E in Comparative Example 6 was used, and the compound (5-1-1) in a weight ratio of 0.10 was added thereto. A liquid crystal film was formed in the same manner as in Example 3 except that the polymerizable liquid crystal composition (G) was used, and the liquid crystal film exhibited a random alignment.

Comparative Example 8

The compounds (1-1-A2), (3-1-G2) and (4-1-A1) were mixed at a ratio (1-1-A2)/(3-1-G2)/(4-1-A1)=35/35/30 by weight to prepare a mixture MIX-F, and a polymerizable liquid crystal composition (H) was prepared in the same manner as in Example 11 except that MIX-F was used, and the compound (5-1-1) was not added. A liquid crystal film was formed in the same manner as in Example 3 except that the polymerizable liquid crystal composition (H) was used, and the liquid crystal film exhibited a random alignment.

Comparative Example 9

A polymerizable liquid crystal composition (I) was prepared in the same manner as in Example 11 except that MIX-F in Comparative Example 8 was used, and the compound (5-1-1) in a weight ratio of 0.10 was added thereto. A liquid crystal film was formed in the same manner as in Example 3 except that the polymerizable liquid crystal composition (I) was used, and the liquid crystal film exhibited a random alignment.

It is understood from the results of Examples and Comparative Examples that the liquid crystal films exhibiting a uniform homeotropic alignment can be obtained from a polymerizable liquid crystal composition containing a polymerizable triptycene derivative, a polymerizable compound having a bisphenol skeleton and a silane coupling agent.

INDUSTRIAL APPLICABILITY

According to the invention, a polymerizable liquid crystal composition containing a polymerizable triptycene derivative provides a liquid crystal film exhibiting a uniform homeotropic alignment independently from kind of a supporting substrate without a special alignment film, and enables control of the birefringence thereof. 

The invention claimed is:
 1. A polymerizable liquid crystal composition comprising a mixture of polymerizable compounds containing at least one compound selected from a group of compounds represented by the formula (1-1) as a component A, at least one compound selected from a group of compounds represented by the formula (2-1) or at least one compound selected from a group of compounds represented by the formulae (2-2) to (2-4) as a component B, at least one compound selected from a group of compounds represented by the formula (3-1) as a component C and at least one compound selected from a group of compounds represented by the formulae (4-1) to (4-3) as a component D, and at least one compound selected from a group of compounds represented by the formulae (5-1) and (5-2) as a component E:

wherein in the formula (1-1), ring T represents triptycen-1,4-diyl; Z¹ independently represents hydrogen, fluorine, chlorine, methyl or trifluoromethyl; W¹ independently represents hydrogen, halogen, alkyl having from 1 to 3 carbon atoms or fluoroalkyl having from 1 to 3 carbon atoms; Y¹ independently represents a single bond, —COO—, —OCO—, —CH═CH—COO—, —OCO—CH═CH—, —(CH₂)₂—COO— or —OCO—(CH₂)₂—; and n1 independently represents an integer of from 2 to 15, in the formula (2-1), Z² independently represents hydrogen, fluorine, methyl or trifluoromethyl; W² independently represents hydrogen, halogen, alkyl having from 1 to 3 carbon atoms or fluoroalkyl having from 1 to 3 carbon atoms; Y² independently represents a single bond, —CH═CH— or —(CH₂)₂—; and n2 independently represents an integer of from 2 to 15, in the formula (2-2), L^(1a) and L^(1b) each independently represent alkyl having from 1 to 4 carbon atoms; R^(2a) and R^(2b) each independently represent alkylene having from 2 to 4 carbon atoms; Z²² independently represents hydrogen or methyl; k1 and k2 each independently represent an integer of from 0 to 4; and m22 and n22 each independently represent an integer of from 0 to 6, in the formula (2-3), Z²³ independently represents hydrogen or methyl; R^(3a) and R^(3b) each independently represent hydrogen, methyl or ethyl; and m23 and n23 each independently represent an integer of from 0 to 3, in the formula (2-4), Z²⁴ independently represents hydrogen or methyl; R^(4a) and Rob each independently represent hydrogen or alkyl having from 1 to 6 carbon atoms; L^(2a) and L^(2b) each independently represent alkyl having from 1 to 6 carbon atoms; m24 and n24 each independently represent an integer of from 1 to 3; m25 and n25 each independently represent an integer of from 1 to 3; and j1 and j2 each independently represent an integer of from 0 to 4, in the formula (3-1), Z³ represents hydrogen, fluorine, methyl or trifluoromethyl; W³ independently represents hydrogen, halogen, alkyl having from 1 to 3 carbon atoms or fluoroalkyl having from 1 to 3 carbon atoms; X³ represents a single bond, —O—, alkylene having from 1 to 20 carbon atoms, —COO— or —OCO—; ring A³ represents 1,4-phenylene or 1,4-cyclohexylene; R³ represents hydrogen, fluorine, chlorine, cyano, alkyl having from 1 to 20 carbon atoms or alkoxy having from 1 to 20 carbon atoms, in which in the alkyl and the alkoxy, arbitrary hydrogen may be replaced by fluorine; n3 represents an integer of from 0 to 20; and p and q each independently represent 0 or 1, provided that when n3 is 0, X³ represents a single bond or alkylene having from 1 to 20 carbon atoms, in the formulae (4-1) to (4-3), Z⁴ independently represents hydrogen, fluorine, methyl or trifluoromethyl; W⁴ independently represents hydrogen, halogen, alkyl having from 1 to 3 carbon atoms or fluoroalkyl having from 1 to 3 carbon atoms; W⁴¹ independently represents hydrogen, halogen, alkyl having from 1 to 3 carbon atoms or fluoroalkyl having from 1 to 3 carbon atoms; W⁴² independently represents hydrogen, halogen, alkyl having from 1 to 8 carbon atoms or fluoroalkyl having from 1 to 3 carbon atoms; ring A⁴ independently represents 1,4-phenylene or 1,4-cyclohexylene; X⁴¹ and X⁴² each independently represent a single bond, —COO—, —OCO—, —CH═CH—COO—, —OCO—CH═CH—, —(CH₂)₂—COO—, —OCO—(CH₂)₂—, —(CH₂)₂—, —CH₂O— or —OCH₂—; r represents 0 or 1; Y⁴ independently represents a single bond, alkylene having from 1 to 20 carbon atoms, —O—, —COO—, —OCO— or —OCOO—; and n4 independently represents an integer of from 0 to 20, provided that when n4 is 0, Y⁴ represents a single bond or alkylene having from 1 to 20 carbon atoms, in the formulae (5-1) and (5-2), R⁵ independently represents methyl or ethyl; n5 represents an integer of from 1 to 5; R⁵¹ represents alkyl having from 1 to 4 carbon atoms; m represents an integer of from 1 to 3; Y⁵ represents alkylene having from 1 to 10 carbon atoms; R⁵² represents hydrogen or alkyl having from 1 to 10 carbon atoms; and R⁵³ represents alkyl having from 1 to 10 carbon atoms, and in the formula (2-1), A² represents a divalent group represented by one of the formulae (A2-1) to (A2-19):


2. The polymerizable liquid crystal composition according to claim 1, wherein: in the formula (1-1), ring T represents triptycen-1,4-diyl; Z¹ independently represents hydrogen, fluorine, methyl or trifluoromethyl; W¹ independently represents hydrogen, fluorine, methyl or trifluoromethyl; Y¹ independently represents —COO—, —OCO—, —CH═CH—COO—, —OCO—CH═CH—, —(CH₂)₂—COO— or —OCO—(CH₂)₂—; and n1 independently represents an integer of from 2 to 10, in the formula (2-1), A² represents a divalent group represented by one of the formulae (A2-1) to (A2-18); Z² independently represents hydrogen, fluorine, methyl or trifluoromethyl; W² independently represents hydrogen or fluorine; Y² independently represents a single bond, —CH═CH— or —(CH₂)₂—; and n2 independently represents an integer of from 2 to 10, in the formula (2-2), k1 and k2 are both 0; R^(2a) and R^(2b) each independently represent alkylene having from 2 to 4 carbon atoms; Z²² independently represents hydrogen or methyl; and m22 and n22 each independently represent an integer of from 0 to 6, in the formula (2-3), Z²³ independently represents hydrogen or methyl; R^(3a) and R^(3b) each independently represent hydrogen, methyl or ethyl; and m23 and n23 each independently represent an integer of from 0 to 3, in the formula (2-4), j1 and j2 are both 0; Z²⁴ independently represents hydrogen or methyl; R^(4a) and R^(4b) each represent hydrogen; m24 and n24 each independently represent an integer of from 1 to 3; and m25 and n25 each independently represent an integer of from 1 to 3, in the formula (3-1), Z³ represents hydrogen, fluorine, methyl or trifluoromethyl; W³ independently represents hydrogen, fluorine, methyl or trifluoromethyl; X³ represents a single bond or —O—; ring A³ represents 1,4-phenylene or 1,4-cyclohexylene; R³ represents cyano, alkyl having from 1 to 10 carbon atoms or alkoxy having from 1 to 10 carbon atoms, in which in the alkyl and the alkoxy, arbitrary hydrogen may be replaced by fluorine; n3 represents an integer of from 2 to 12; and p and q each independently represent 0 or 1, in the formulae (4-1) to (4-3), Z⁴ independently represents hydrogen, fluorine, methyl or trifluoromethyl; W⁴ independently represents hydrogen, fluorine, methyl or trifluoromethyl; W⁴¹ independently represents hydrogen, methyl or ethyl; W⁴² independently represents hydrogen, alkyl having from 1 to 6 carbon atoms or trifluoromethyl; ring A⁴ independently represents 1,4-phenylene or 1,4-cyclohexylene; X⁴¹ and X⁴² each independently represent a single bond, —COO—, —OCO—, —CH═CH—COO—, —OCO—CH═CH—, —(CH₂)₂—COO— or —OCO—(CH₂)₂—; r represents 0 or 1; Y⁴ independently represents a single bond, —O—, —COO—, —OCO— or —OCOO—; and n4 independently represents an integer of from 2 to 12, in the formulae (5-1) and (5-2), R⁵ independently represents methyl or ethyl; n5 represents an integer of from 1 to 5; R⁵¹ represents alkyl having from 1 to 4 carbon atoms; m represents an integer of from 1 to 3; Y⁵ represents alkylene having from 1 to 10 carbon atoms; R⁵² represents hydrogen or alkyl having from 1 to 10 carbon atoms; and R⁵³ represents alkyl having from 1 to 10 carbon atoms, a ratio of the component A is from 10 to 55% by weight, a ratio of the component B is from 3 to 20% by weight, a ratio of the component C is from 10 to 50% by weight, and a ratio of the component D is from 10 to 77% by weight, based on a total weight of the mixture of polymerizable compounds containing the components A to D, and a ratio of the component E is from 0.01 to 0.20 in terms of weight ratio based on the mixture.
 3. The polymerizable liquid crystal composition according to claim 1, wherein: in the formula (1-1), ring T represents triptycen-1,4-diyl; Z¹ independently represents hydrogen, fluorine, methyl or trifluoromethyl; W¹ independently represents hydrogen or fluorine; Y¹ independently represents —COO— or —OCO—; and n1 independently represents an integer of from 2 to 8, in the formula (2-1), A² represents a divalent group represented by one of the formulae (A2-1) to (A2-18); Z² independently represents hydrogen or methyl; W² independently represents hydrogen or fluorine; Y² independently represents a single bond, —CH═CH— or —(CH₂)₂—; and n2 independently represents an integer of from 2 to 8, in the formula (2-2), k1 and k2 are both 0; R^(2a) and R^(2b) each independently represent alkylene having from 2 to 4 carbon atoms; Z²² represents hydrogen; and m22 and n22 each independently represent an integer of from 0 to 6, in the formula (2-3), Z²³ represents hydrogen; R^(3a) and R^(3b) each represent hydrogen; and m23 and n23 each independently represent an integer of from 0 to 3, in the formula (2-4), j1 and j2 are both 0; Z²⁴ represents hydrogen; R^(4a) and R^(4b) each represent hydrogen; m24 and n24 each independently represent an integer of from 1 to 3; and m25 and n25 each independently represent an integer of from 1 to 3, in the formula (3-1), Z³ represents hydrogen or methyl; W³ independently represents hydrogen or fluorine; X³ represents a single bond or —O—; ring A³ represents 1,4-phenylene or 1,4-cyclohexylene; R³ represents cyano, alkyl having from 1 to 10 carbon atoms or alkoxy having from 1 to 10 carbon atoms, in which in the alkyl and the alkoxy, arbitrary hydrogen may be replaced by fluorine; n3 represents an integer of from 2 to 10; and p and q each independently represent 0 or 1, in the formulae (4-1) to (4-3), Z⁴ independently represents hydrogen or methyl; W⁴ independently represents hydrogen, fluorine, methyl or trifluoromethyl; W⁴¹ independently represents hydrogen or methyl; W⁴² independently represents hydrogen, alkyl having from 1 to 4 carbon atoms or trifluoromethyl; ring A⁴ represents 1,4-phenylene or 1,4-cyclohexylene; X⁴¹ and X⁴² each independently represent —COO—, —OCO—, —CH═CH—COO—, —OCO—CH═CH—, —(CH₂)₂—COO— or —OCO—(CH₂)₂—; r represents 0 or 1; Y⁴ independently represents a single bond, —O—, —COO—, —OCO— or —OCOO—; and n4 independently represents an integer of from 2 to 12, in the formulae (5-1) and (5-2), R⁵ independently represents methyl or ethyl; n5 represents an integer of from 1 to 5; R⁵¹ represents alkyl having from 1 to 4 carbon atoms; m represents an integer of from 1 to 3; Y⁵ represents alkylene having from 1 to 10 carbon atoms; R⁵² represents hydrogen or alkyl having from 1 to 10 carbon atoms; and R⁵³ represents alkyl having from 1 to 10 carbon atoms, a ratio of the component A is from 15 to 55% by weight, a ratio of the component B is from 3 to 15% by weight, a ratio of the component C is from 15 to 45% by weight, and a ratio of the component D is from 15 to 67% by weight, based on a total weight of the mixture of polymerizable compounds containing the components A to D, and a ratio of the component E is from 0.03 to 0.15 in terms of weight ratio based on the mixture.
 4. The polymerizable liquid crystal composition according to claim 1, wherein: in the formula (1-1), ring T represents triptycen-1,4-diyl; Z¹ represents hydrogen; W¹ independently represents hydrogen or fluorine; Y¹ independently represents —COO— or —OCO—; and n1 independently represents an integer of from 4 to 6, in the formula (2-1), A² represents a divalent group represented by one of the formulae (A2-1), (A2-4), (A2-10), (A2-11) and (A2-16); Z² represents hydrogen; W² independently represents hydrogen or fluorine; Y² independently represents a single bond, —CH═CH— or —(CH₂)₂—; and n2 independently represents an integer of from 4 to 6, in the formula (2-2), k1 and k2 are both 0; R^(2a) and R^(2b) each independently represent alkylene having from 2 to 4 carbon atoms; Z²² represents hydrogen; and m22 and n22 each independently represent an integer of from 0 to 6, in the formula (2-3), Z²³ represents hydrogen; R^(3a) and R^(3b) each represent hydrogen; and m23 and n23 each independently represent an integer of from 0 to 3, in the formula (2-4), j1 and j2 are both 0; Z²⁴ represents hydrogen; R^(4a) and R^(4b) each represent hydrogen; m24 and n24 each independently represent an integer of from 1 to 3; and m25 and n25 each independently represent an integer of from 1 to 3, in the formula (3-1), Z³ represents hydrogen; W³ represents hydrogen; X³ represents a single bond or —O—; ring A³ represents 1,4-phenylene; R³ represents cyano; n3 represents an integer of from 4 to 6; and p and q each independently represent 0 or 1, in the formulae (4-1) to (4-3), Z⁴ represents hydrogen; W⁴ independently represents hydrogen, fluorine or methyl; W⁴¹ independently represents hydrogen or methyl; W⁴² independently represents hydrogen, methyl or trifluoromethyl; ring A⁴ represents 1,4-phenylene; X⁴¹ and X⁴² each independently represent —COO—, —OCO—, —CH═CH—COO—, —OCO—CH═CH—, —(CH₂)₂—COO— or —OCO—(CH₂)₂—; r represents 0 or 1; Y⁴ independently represents a single bond or —O—; and n4 independently represents an integer of from 4 to 6, in the formulae (5-1) and (5-2), R⁵ independently represents methyl or ethyl; n5 represents an integer of from 1 to 5; R⁵¹ represents alkyl having from 1 to 4 carbon atoms; m represents an integer of from 1 to 3; Y⁵ represents alkylene having from 1 to 10 carbon atoms; R⁵² represents hydrogen or alkyl having from 1 to 10 carbon atoms; and R⁵³ represents alkyl having from 1 to 10 carbon atoms, a ratio of the component A is from 20 to 45% by weight, a ratio of the component B is from 8 to 12% by weight, a ratio of the component C is from 20 to 40% by weight, and a ratio of the component D is from 20 to 52% by weight, based on a total weight of the mixture of polymerizable compounds containing the components A to D, and a ratio of the component E is from 0.05 to 0.15 in terms of weight ratio based on the mixture.
 5. The polymerizable liquid crystal composition according to claim 1, wherein: in the formula (1-1), ring T represents triptycen-1,4-diyl; Z¹ represents hydrogen; W¹ independently represents hydrogen or fluorine; Y¹ independently represents —COO— or —OCO—; and n1 independently represents an integer of from 4 to 6, in the formula (2-1), A² represents a divalent group represented by one of the formulae (A2-10) and (A2-16); Z² represents hydrogen; W² independently represents hydrogen or fluorine; Y² independently represents a single bond, —CH═CH— or —(CH₂)₂—; and n2 independently represents an integer of from 4 to 6, in the formula (2-2), k1 and k2 are both 0; R^(2a) and R^(2b) each independently represent alkylene having from 2 to 4 carbon atoms; Z²² represents hydrogen; and m22 and n22 each independently represent an integer of from 1 to 4, in the formula (2-3), Z²³ represents hydrogen; R^(3a) and R^(3b) each represent hydrogen; and m23 and n23 each independently represent an integer of from 0 to 3, in the formula (2-4), j1 and j2 are both 0; Z²⁴ represents hydrogen; R^(4a) and R^(4b) each represent hydrogen; m24 and n24 each independently represent an integer of from 1 to 3; and m25 and n25 each independently represent an integer of from 1 to 3, in the formula (3-1), Z³ represents hydrogen; W³ represents hydrogen; X³ represents a single bond or —O—; ring A³ represents 1,4-phenylene; R³ represents cyano; n3 represents an integer of from 4 to 6; and p and q each independently represent 0 or 1, in the formulae (4-1) to (4-3), Z⁴ represents hydrogen; W⁴ independently represents hydrogen, fluorine or methyl; W⁴¹ independently represents hydrogen or methyl; W⁴² independently represents hydrogen, methyl or trifluoromethyl; ring A⁴ represents 1,4-phenylene; X⁴¹ and X⁴² each independently represent —COO—, —OCO—, —CH═CH—COO—, —OCO—CH═CH—, —(CH₂)₂—COO— or —OCO—(CH₂)₂—; r represents 0 or 1; Y⁴ independently represents a single bond or —O—; and n4 independently represents an integer of from 4 to 6, in the formulae (5-1) and (5-2), R⁵ independently represents methyl or ethyl; n5 represents an integer of from 1 to 5; R⁵¹ represents alkyl having from 1 to 4 carbon atoms; m represents an integer of from 1 to 3; Y⁵ represents alkylene having from 1 to 10 carbon atoms; R⁵² represents hydrogen or alkyl having from 1 to 10 carbon atoms; and R⁵³ represents alkyl having from 1 to 10 carbon atoms, a ratio of the component A is from 20 to 45% by weight, a ratio of the component B is from 8 to 12% by weight, a ratio of the component C is from 20 to 40% by weight, and a ratio of the component D is from 20 to 52% by weight, based on a total weight of the mixture of polymerizable compounds containing the components A to D, and a ratio of the component E is from 0.07 to 0.15 in terms of weight ratio based on the mixture.
 6. The polymerizable liquid crystal composition according to claim 1, wherein: in the formulae (5-1) and (5-2), R⁵ represents ethyl; n5 represents an integer of from 1 to 5; R⁵¹ represents methyl or ethyl; m represents 3; Y⁵ represents alkylene having from 1 to 10 carbon atoms; R⁵² represents hydrogen or alkyl having from 1 to 10 carbon atoms; and R⁵³ represents alkyl having from 1 to 10 carbon atoms.
 7. The polymerizable liquid crystal composition according to claim 2, wherein: in the formulae (5-1) and (5-2), R⁵ represents ethyl; n5 represents an integer of from 1 to 5; R⁵¹ represents methyl or ethyl; m represents 3; Y⁵ represents alkylene having from 1 to 10 carbon atoms; R⁵² represents hydrogen or alkyl having from 1 to 10 carbon atoms; and R⁵³ represents alkyl having from 1 to 10 carbon atoms, and a ratio of the component E is from 0.07 to 0.13 in terms of weight ratio based on the mixture of polymerizable compounds containing the components A to D.
 8. A polymerizable liquid crystal layer having a homeotropic alignment obtained by directly coating the polymerizable liquid crystal composition according to claim 1 on a supporting substrate.
 9. The polymerizable liquid crystal layer according to claim 8, wherein the supporting substrate is a glass substrate.
 10. The polymerizable liquid crystal layer according to claim 8, wherein the supporting substrate is a glass substrate plated with a plastic thin film, or a plastic film substrate.
 11. The polymerizable liquid crystal layer according to claim 8, wherein the supporting substrate is a glass substrate which is plated with a plastic thin film and then the surface of the plastic thin film is subjected to a rubbing treatment, a corona treatment or a plasma treatment, or a plastic film substrate having a surface subjected to a rubbing treatment, a corona treatment or a plasma treatment.
 12. The polymerizable liquid crystal layer according to claim 10, wherein a plastic material constituting the plastic thin film or the plastic film is one selected from polyimide, polyamideimide, polyamide, polyetherimide, polyetheretherketone, polyetherketone, polyketonesulfide, polyethersulfone, polysulfone, polyphenylene sulfide, polyphenylene oxide, polyethylene terephthalate, polybutylene terephthalate, polyethylene naphthalate, polyacetal, polycarbonate, polyarylate, an acrylic resin, polyvinyl alcohol, polypropylene, cellulose, triacetyl cellulose, a partially saponified product of triacetyl cellulose, an epoxy resin, a phenol resin and a cycloolefin resin.
 13. The polymerizable liquid crystal layer according to claim 12, wherein a plastic material constituting the plastic thin film or the plastic film is one selected from polyimide, polyvinyl alcohol, triacetyl cellulose, a partially saponified product of triacetyl cellulose and a cycloolefin resin.
 14. A liquid crystal film having a homeotropic alignment obtained by polymerizing the polymerizable liquid crystal layer according to claim
 8. 15. An optical compensation device comprising the liquid crystal film according to claim
 14. 16. An optical device comprising the liquid crystal film according to claim 14 and a polarizing plate.
 17. A liquid crystal display device comprising the optical compensation device according to claim 15 on an inner surface or an outer surface of a liquid crystal cell.
 18. A liquid crystal display device comprising the optical device according to claim 16 on an outer surface of a liquid crystal cell. 